The determination of critical pitting temperatures (CPT) in various test solutions like ferric chloride solution according to ASTM G48 or 'Green Death' solution is a common test method for the comparative assessment of the pitting corrosion resistance of highly alloyed steels and Ni–Cr–Mo alloys. In addition to the well-known disadvantages of standard methods, like long test times, subjective examination, and large scatter, for the highest alloyed Ni–Cr–Mo alloys no stable pitting corrosion can initiate even at the highest test temperatures. This paper describes the limitations of standard test methods and shows how these problems can be solved by an alternative test solution and an adjusted test method. By capturing and examining the current noise under potentiostatic conditions during continuous heating in a 4.5 M calcium chloride solution the transition from metastable to stable pitting corrosion as a criterion for CPT can be detected in a reproducible way.
Ageing at 600 °C (from 0.1 h up to 20 h) leads to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries of the lean duplex stainless steel (LDSS) X2CrNiN22-2. This leads to sensitisation due to chromium depletion and decreased pitting corrosion resistance proven by the results of various electrochemical methods (DL-EPR and determination of CPT, Epit). These results were compared with the KorroPad method, which uses an agar-based gel-electrolyte for the detection of stainless steel surfaces prone to pitting corrosion. However, the standard configuration of the KorroPad showed no differentiation for the various ageing conditions. Therefore, modified versions of the KorroPad with two, five and ten times higher NaCl and potassium ferrocyanide III (K3[Fe(CN)6]) concentrations were successfully used to visualise the behaviour detected by DL-EPR, Epit and CPT. Therefore, the KorroPad method can also detect a microstructure related reduction of pitting corrosion resistance, which can drastically reduce the experimental effort to generate sensitisation diagrams for stainless steels.