The fire behaviour of carbon fibre (CF) reinforced polymers differs in comparison to polymers. Fibres behave often inert with respect to pyrolysis, they change the melt flow and dripping behaviour, the heat absorption and transfer, the amount and properties of the fire residue and so on. Flame and fire retardancy concepts are needed not only suitable for the different fire protection goals typical for each application, but also tailored for composites. This field is illuminated by examples taken from different projects carried out in the group of the author in the recent years. The examples target on different applications through achieving reduction in reaction to fire controlling the fire risks (flammability, heat release) in the beginning and development of a fire and investigating the fire stability, when a severe flame is directly applied (key property in fully developed fires). Approaches to halogen-free flame retardancy in CF reinforced thermosets are presented as well as building up a bench and an intermediate scale testing of composites in fire applying mechanical load (up to 1 MN compression) and direct flame exposure (180 kW/m2) simultaneously. Indeed, e.g. we have investigated the fire stability of stringer reinforced shell components taken out from the fuselage of an aircraft.
The understanding of fire behaviour, fire resistance, and fire retardant modes of action in composites is a promising basis for target-oriented development. The role of flame inhibition, charring, and protective layer formation is discussed. Successful concepts are presented for fire retardancy tailored for different application as well as general guidelines for future development. Different phosphorus flame retardants are proposed to achieve halogen-free flame retardancy with respect to ignition and developing fires. Different protective approaches are sketched for addressing the fire stability of composites that is the most important fire risk for the fire resistance in structural applications.
The effectiveness of distinct fillers, from micro to nano-size scaled, on the fire behaviour of an epoxy resin and its carbon fibre reinforced composites was assessed by cone calorimetry. The performance was compared not only regarding the reaction to fire performance, but also in terms of thermal stability, glass transition temperature and microstructure. Regarding the fire reaction behaviour of nanofilled epoxy resin, anionic nanoclays and thermally oxidized carbon nanotubes showed the best results, in agreement with more compact chars formed on the surface of the burning polymer. For carbon fibre reinforced composite plates, the cone calorimeter results of modified resin samples did not show significant improvements on the heat release rate curves. Poorly dispersed fillers in the resin additionally caused reductions on the glass transition temperature of the composite materials.