Textile, aluminium and polyethylene used as components in laser protection curtains were investigated with respect to their ablation behaviour. Employing 33-fs pulses (800 nm wavelength, 1 kHz repetition rate), ex situ geometrical measurements of the ablation cavities and in situ acoustic investigations with a microphone were performed to determine the ablation thresholds in the single- and multi-pulse cases. The acoustical method proved advantageous for complex surface morphologies and/or single laser pulse interactions. Incubation phenomena can be observed for all the materials studied. Technically relevant multi-pulse ablation thresholds are presented and are compared with the single-pulse (1-on-1) irradiation.
Ablation experiments employing Ti:sapphire laser pulses with durations from 30 to 340 fs (centre wavelength 800 nm, repetition rate 1 kHz) were performed in air. Absorbing filters (Schott BG18 and BG36) served as targets. The direct focusing technique was used under single- and multi-pulse irradiation conditions. Ablation threshold fluences were determined from a semi-logarithmic plot of the ablation crater diameter versus laser fluence. The threshold fluence decreases for a shorter pulse duration and an increasing number of pulses. The multi-pulse ablation threshold fluences are similar to those of undoped glass material (~1 J cm-2). That means that the multi-pulse ablation threshold is independent on the doping level of the filters. For more than 100 pulses per spot and all pulse durations applied, the threshold fluence is practically constant. This leads to technically relevant ablation threshold values.
Damage experiments of absorbing filters (Schott BG18 and BG36) were performed with Ti:sapphire laser pulses with durations from 30 fs to 340 fs (800 nm, 1 kHz) in air. The direct focusing technique was employed under single- and multi-pulse irradiation conditions. Ablation threshold fluences were determined from a semi-logarithmic plot of the ablation crater diameter vs. laser fluence. The damage threshold fluence decreases for shorter pulse durations. In the investigated pulse duration range, the measured multi-pulse ablation threshold fluences are practically similar to those of undoped glass material (~1 Jcm-2). That means that the multi-pulse ablation threshold is independent on the doping level of the filters. For more than 100 pulses per spot and all pulse durations applied, the threshold fluence saturates. This leads to technically relevant damage threshold values in the femtosecond laser pulse duration domain.
Optical filters and fabrics are important parts of laser safety equipment such as goggles and curtains. A choice of these materials with varying absorption spectra is investigated with respect to their resistance to Ti:sapphire femtosecond laser radiation (800 nm wavelength, 1 kHz repetition rate). Pulse durations down to 30 fs and multiple-pulse irradiation conditions are employed to evaluate technically relevant damage thresholds. The ablation threshold fluences of the absorbing filters are comparable to those observed for transparent materials with 30-fs-pulses. These investigations together with scanning electron microscopy of the surface morphology after laser treatment provide insight into the interaction mechanism of the short pulses with the materials.
Commercially available absorption filters (Schott BG18 and BG36) were investigated with respect to their single- and
multi-pulse ablation threshold using laser pulses from a Ti:Sapphire laser in the range between 30 and 340 fs. It could be
observed, that the threshold fluence decreases for shorter pulse durations. The similarity of the measured multi-pulse
threshold fluences with those of undoped glass material (around 1 J/cm^2 for a pulse duration of 30 fs) suggests that, for
very short pulses, the threshold is independent on the doping level and therefore, linear absorption does not significantly
contribute to laser-induced damage. For >100 pulses per spot and all pulse durations applied, the threshold fluences
saturate. This independence on the number of applied pulses leads to technically relevant damage threshold values.