Solubility and ingrowth behaviour of degradable and figuline calcium alkaline phosphate cements

  • The thrust of the investigations presented here is to point out the degradation behaviour in vitro and the ingrowth behaviour in vivo of four different calcium alkaline phosphate cements. Two of the figuline and mouldable composites consist of the crystalline phase Ca2KNa(PO4)2 and two of the crystalline phase Ca10[K/Na](PO4)2 each containing 2wt% medium gel strength porcine gelatin. Furthermore A-TCP was added to both Ca10[K/Na](PO4)2 cements as a hardening supporting reactant. The testing material groups differ in small amorphous portions containing either silica phosphate (GB9), magnesium potassium phosphate (GB14) or diphosphates (401545 and 401545(70)). The respective composites show a monomodal particle size distribution (d50~7µm; span~4) and an average total porosity around 28vol%.For the solubility studies cylindrical samples (d=6mm; h=12mm) were stored in a 0.1mol TRIS buffer solution and incubated at 37°C for maximum 50 weeks. The storage solution was analysed and renewedThe thrust of the investigations presented here is to point out the degradation behaviour in vitro and the ingrowth behaviour in vivo of four different calcium alkaline phosphate cements. Two of the figuline and mouldable composites consist of the crystalline phase Ca2KNa(PO4)2 and two of the crystalline phase Ca10[K/Na](PO4)2 each containing 2wt% medium gel strength porcine gelatin. Furthermore A-TCP was added to both Ca10[K/Na](PO4)2 cements as a hardening supporting reactant. The testing material groups differ in small amorphous portions containing either silica phosphate (GB9), magnesium potassium phosphate (GB14) or diphosphates (401545 and 401545(70)). The respective composites show a monomodal particle size distribution (d50~7µm; span~4) and an average total porosity around 28vol%.For the solubility studies cylindrical samples (d=6mm; h=12mm) were stored in a 0.1mol TRIS buffer solution and incubated at 37°C for maximum 50 weeks. The storage solution was analysed and renewed every week. The results are plotted cumulative. For the in vivo studies critical size defects were dissected to mandibles in a sheep model in which a 1cm³ area of the bottom of the mandibles was surgically resected and replaced with the figuline cements whereas the mouldability allows the reconstruction of the original outer contour without draining off even when replacing upside down.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Felix Dombrowski, Heidi Marx, Ute Ploska, Dagmar Nicolaides, M. Stiller, C. Knabe, Georg Berger
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Key engineering materials
Jahr der Erstveröffentlichung:2012
Verlag:Trans Tech Publ.
Verlagsort:Aedermannsdorf
Jahrgang/Band:493-494
Erste Seite:387
Letzte Seite:390
Freie Schlagwörter:Calcium alkaline phosphate cement; Figuline; Gelatin; Ingrowth behavior; Solubility
DOI:10.4028/www.scientific.net/KEM.493-494.387
ISSN:1013-9826
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:05.12.2011
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.