• Treffer 6 von 28
Zurück zur Trefferliste

Influences on the tribological behaviour of slip-rolling DLC-coatings

  • Diamond like carbon (DLC)-coatings are applied very successfully on computer discs. Sliding friction tests confirm their high performance as dry lubricants with friction coefficients (COFs) below 0.1. In contrast to sliding tests, until very recently most of the DLC-coatings failed in slip-rolling test after fewer cycles than uncoated samples. However, present tests with DLC-coatings of seven different suppliers show a more promising tribological behaviour under slip-rolling conditions. The DLC-coatings were deposited onto steel 100Cr6, HRC 60, with a thickness of 2–3 ?m. The counter bodies were uncoated, grinded or polished 100Cr6 discs with 30 mm radius of curvature. The tests were performed on a twin disc testing rig (Amsler type) with paraffin oil under boundary/mixed lubrication and rolling with 10% slip. The initial, average Hertzian contact pressure was adjusted to Pm = 1.0, 1.25, and 1.5 GPa. The failure criterion was defined as the occurrence of a single damaged area largerDiamond like carbon (DLC)-coatings are applied very successfully on computer discs. Sliding friction tests confirm their high performance as dry lubricants with friction coefficients (COFs) below 0.1. In contrast to sliding tests, until very recently most of the DLC-coatings failed in slip-rolling test after fewer cycles than uncoated samples. However, present tests with DLC-coatings of seven different suppliers show a more promising tribological behaviour under slip-rolling conditions. The DLC-coatings were deposited onto steel 100Cr6, HRC 60, with a thickness of 2–3 ?m. The counter bodies were uncoated, grinded or polished 100Cr6 discs with 30 mm radius of curvature. The tests were performed on a twin disc testing rig (Amsler type) with paraffin oil under boundary/mixed lubrication and rolling with 10% slip. The initial, average Hertzian contact pressure was adjusted to Pm = 1.0, 1.25, and 1.5 GPa. The failure criterion was defined as the occurrence of a single damaged area larger than 1 mm2, which was controlled by optical microscopy (OM). An acoustic emission (AE) measurement system was installed as an additional online control for coating failure. The stressed coatings and the chipping areas were analyzed by OM, SEM, EDX, AFM and Raman spectroscopy. Until now, the results reveal that a large scatter in lifetime of coatings occurs not only between samples of different coaters but also between the samples of one single batch. The highest lifetime reached by a DLC-coating under these testing conditions is 10 × 106 cycles. That is the highest life time for a coating tested under the testing conditions above in our laboratory so far. The following factors were identified to influence the life time of the coatings: coating thickness, interlayer type, topography of the coatings, counter body roughness and mechanical properties. But the most important factor determining the life time of the coatings is that the coating process does produce homogenous layers free of faults.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Dieter Klaffke, Erich Santner, Dirk SpaltmannORCiD, Mathias WoydtORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Wear
Jahr der Erstveröffentlichung:2005
Verlag:Elsevier
Verlagsort:Amsterdam
Jahrgang/Band:259
Erste Seite:752
Letzte Seite:758
Freie Schlagwörter:Acoustic emission; DLC-coatings; Life time; Slip-rolling
DOI:10.1016/j.wear.2005.01.008
ISSN:0043-1648
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:13.06.2005
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.