- Costs reduction is one of the major objectives in mechanical applications with a parallel increase of the power output. Another driver represents new environmental standards and their increasing restrictions in the automotive industry leading to the question, if materials based concepts may substitute harmful EP/AW additives in lubricants. This paper presents the slip-rolling resistance of different DLC/THC coatings on steel substrates with a definite slip rate of 10%. Industrial DLC coatings of ta-C and a-C:H types from various manufacturers were deposited on steels SAE 52100 and AMS 5898 to compile the slip-rolling resistance under initial average Hertzian contact pressures between 1.5 GPa and 2 GPa. The tests were carried out on Amsler-type twin disc tribometer under the regime of mixed/boundary lubrication in unadditivated paraffinic oil (ISO VG 46) and a factory fill engine oil. The spherical steel sample was uncoated and the cylindrical coated with DLC. Some coatings achieved 10Costs reduction is one of the major objectives in mechanical applications with a parallel increase of the power output. Another driver represents new environmental standards and their increasing restrictions in the automotive industry leading to the question, if materials based concepts may substitute harmful EP/AW additives in lubricants. This paper presents the slip-rolling resistance of different DLC/THC coatings on steel substrates with a definite slip rate of 10%. Industrial DLC coatings of ta-C and a-C:H types from various manufacturers were deposited on steels SAE 52100 and AMS 5898 to compile the slip-rolling resistance under initial average Hertzian contact pressures between 1.5 GPa and 2 GPa. The tests were carried out on Amsler-type twin disc tribometer under the regime of mixed/boundary lubrication in unadditivated paraffinic oil (ISO VG 46) and a factory fill engine oil. The spherical steel sample was uncoated and the cylindrical coated with DLC. Some coatings achieved 10 million cycles without any damage under a maximal Hertzian contact pressure Pmax well over 2.25 GPa, thus exceeding FZG 12.…