Damage of stainless steel bars due to atmospheric corrosion
- In addition to constructional requirements in civil engineering stainless steels often have to fulfil high visual demands. Unexpected impairments of the visual appearance of stainless steels under low corrosive conditions are a widespread problem today. Frequently it is supposed that this is caused by changes in the alloy composition, worse environmental conditions or improper handling. Within a research project the systematic investigation of several cases of damaged stainless steel bars has shown that the reasons are based on well-known material defects like chemical inhomogeneities (e.g. precipitations or local carburization) or geometrical defects (e.g. undercuts, rolling defects or shell formation). Thus, the failures could be clearly identified as production failures of the respective semi-finished products.
Autor*innen: | Andreas Burkert, Jens Lehmann, Annette Burkert, Jürgen Mietz |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Materials and corrosion |
Jahr der Erstveröffentlichung: | 2012 |
Herausgeber (Institution): | Gesellschaft für Korrosionsschutz |
Verlag: | Wiley-VCH Verl. |
Verlagsort: | Weinheim |
Jahrgang/Band: | 63 |
Ausgabe/Heft: | 3 |
Erste Seite: | 264 |
Letzte Seite: | 270 |
Freie Schlagwörter: | Atmospheric corrosion; Dauerhaftigkeit; EPR test; Failure; Intercrystalline corrosion; Korrosion; Nichtrostender Stahl; Stainless steel; Werkstoffauswahl |
DOI: | 10.1002/maco.201005701 |
ISSN: | 0947-5117 |
ISSN: | 1521-4176 |
Verfügbarkeit des Dokuments: | Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access") |
Bibliotheksstandort: | Sonderstandort: Publica-Schrank |
Datum der Freischaltung: | 19.02.2016 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 16.04.2012 |