Femtosecond-pulse visible laser processing of transparent materials

  • High-power lasers in industrial and R & D applications raise the general problem of reliability and degradation of optical components. A systematic study of nonlinear interaction of various transparent dielectric materials as e.g. glasses, fused silica, and polymers, with laser-pulses in the intensity range of up to 1013 W cm-2 is presented. On the other hand, femtosecond-pulse laser processing in the visible spectral range (300 fs; 620 nm, ~ 2 eV) allows precise microstructuring of transparent dielectrics without disruption of the remnant material. Damage and ablation threshold fluences occur above 1.2 J cm-2 at both silicate glasses and fused silica. Two different photon absorption mechanisms have been observed. The first occurs during the initial laser pulses in the incubation range. There, multiphoton absorption results in moderate energy volume densities. These are sufficient to generate morphological changes and optically active defect sites (colour centres) which provide a muchHigh-power lasers in industrial and R & D applications raise the general problem of reliability and degradation of optical components. A systematic study of nonlinear interaction of various transparent dielectric materials as e.g. glasses, fused silica, and polymers, with laser-pulses in the intensity range of up to 1013 W cm-2 is presented. On the other hand, femtosecond-pulse laser processing in the visible spectral range (300 fs; 620 nm, ~ 2 eV) allows precise microstructuring of transparent dielectrics without disruption of the remnant material. Damage and ablation threshold fluences occur above 1.2 J cm-2 at both silicate glasses and fused silica. Two different photon absorption mechanisms have been observed. The first occurs during the initial laser pulses in the incubation range. There, multiphoton absorption results in moderate energy volume densities. These are sufficient to generate morphological changes and optically active defect sites (colour centres) which provide a much higher absorptivity relevant for the second mechanism. It results in gasification without participation of melt.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Jörg KrügerORCiD, Wolfgang Kautek
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Applied surface science
Jahr der Erstveröffentlichung:1996
Verlag:North-Holland
Verlagsort:Amsterdam
Jahrgang/Band:96-98
Erste Seite:430
Letzte Seite:438
ISSN:0169-4332
ISSN:1873-5584
Verfügbarkeit des Dokuments:Weder Datei noch physisches Exemplar vorhanden ("No Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:12.12.2005
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.