Flame retardancy through carbon nanomaterials: carbon black, multiwall nanotubes, expanded graphite, multi layer graphene and graphene in polypropylene

  • Herein we investigate the influence of carbon additives with different particle sizes and shapes on the flame retardancy and mechanical properties of isotactic polypropylene. Thermally reduced graphite oxide (TRGO) and multi-layer graphene (MLG250), consisting of few graphene layers, are compared with spherical, tubular and platelet-like carbon fillers such as carbon black (CB), multiwall nanotubes (MWNT) and expanded graphite (EG). The different morphologies control the dispersion of the carbon particles in PP and play a key role in structure–property relationships. Uniformly dispersed CB, MLG250 and TRGO shift the onset temperature of PP decomposition to temperatures around 30 °C higher, induce a flow limit in the composites' melt viscosity and change drastically their fire behaviour. The prevented dripping and significantly increased heat absorption result in decreased time to ignition and hardly any change in the reaction to a small flame. Under forced-flaming conditions reductionsHerein we investigate the influence of carbon additives with different particle sizes and shapes on the flame retardancy and mechanical properties of isotactic polypropylene. Thermally reduced graphite oxide (TRGO) and multi-layer graphene (MLG250), consisting of few graphene layers, are compared with spherical, tubular and platelet-like carbon fillers such as carbon black (CB), multiwall nanotubes (MWNT) and expanded graphite (EG). The different morphologies control the dispersion of the carbon particles in PP and play a key role in structure–property relationships. Uniformly dispersed CB, MLG250 and TRGO shift the onset temperature of PP decomposition to temperatures around 30 °C higher, induce a flow limit in the composites' melt viscosity and change drastically their fire behaviour. The prevented dripping and significantly increased heat absorption result in decreased time to ignition and hardly any change in the reaction to a small flame. Under forced-flaming conditions reductions in the peak heat release rate of up to 74% are achieved due to the formation of a protective layer of residue during combustion. The described effects of carbon nanomaterials on the properties of PP composites are most pronounced for well-exfoliated graphenes, making them preferable to less exfoliated, micron-sized expanded graphite or conventional spherical and tubular carbon nanoparticles.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Bettina Dittrich, K.-A. Wartig, D. Hofmann, R. Mülhaupt, Bernhard SchartelORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer degradation and stability
Jahr der Erstveröffentlichung:2013
Verlag:Applied Science Publ.
Verlagsort:London
Jahrgang/Band:98
Ausgabe/Heft:8
Erste Seite:1495
Letzte Seite:1505
Freie Schlagwörter:Carbon nanomaterials; Flame retardancy; Graphene; Nanocomposites; Polypropylene; Thermally reduced graphite oxide
DOI:10.1016/j.polymdegradstab.2013.04.009
ISSN:0141-3910
ISSN:1873-2321
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:13.06.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.