Tribological behavior of carbon nanofibers deposited on hard nanocomposite (nc-Ti1 - xAlxN)/(a-Si3N4) coating

  • Main focus was on the deposition of carbon nanofibers (CNFs) onto the hard nanocomposite (nc-Ti1 - xAlxN)/(a-Si3N4) (nACo®) coating surface and the investigation of the structure and tribological properties of CNFs. The alcohol chemical vapor deposition (ACCVD) method was employed to prepare CNFs and the deposition temperatures were 600 and 700 °C, respectively. Prior to the CNF deposition, Ni catalyst was deposited onto the nACo® surface using the magnetron sputtering. The influence of the deposition temperature on the carbon nanofibers structure was investigated by Raman spectroscopy and scanning electron microscopy (SEM). The higher order degree of CNF structure is observed with increasing deposition temperature. Tribological tests were carried out under fretting contact conditions against Al2O3 ball. It is shown that the coefficient of friction (COF) decreases from 1.0 to 1.2 for the clean nACo® surface to 0.2–0.4 for the CNF layers deposited on the nACo® surface. The roughness ofMain focus was on the deposition of carbon nanofibers (CNFs) onto the hard nanocomposite (nc-Ti1 - xAlxN)/(a-Si3N4) (nACo®) coating surface and the investigation of the structure and tribological properties of CNFs. The alcohol chemical vapor deposition (ACCVD) method was employed to prepare CNFs and the deposition temperatures were 600 and 700 °C, respectively. Prior to the CNF deposition, Ni catalyst was deposited onto the nACo® surface using the magnetron sputtering. The influence of the deposition temperature on the carbon nanofibers structure was investigated by Raman spectroscopy and scanning electron microscopy (SEM). The higher order degree of CNF structure is observed with increasing deposition temperature. Tribological tests were carried out under fretting contact conditions against Al2O3 ball. It is shown that the coefficient of friction (COF) decreases from 1.0 to 1.2 for the clean nACo® surface to 0.2–0.4 for the CNF layers deposited on the nACo® surface. The roughness of the nACo® surface was varied and a higher durability of the CNF layers deposited on the rougher nACo® surface is found.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:E. Kimmari, V. Podgursky, M. Simunin, E. Adoberg, A. Surzenkov, M. Viljus, Manfred Hartelt, Rolf WäscheORCiD, I. Sildos, P. Kulu
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Surface and coatings technology
Jahr der Erstveröffentlichung:2013
Verlag:Elsevier Science
Verlagsort:Lausanne
Jahrgang/Band:225
Erste Seite:21
Letzte Seite:25
Freie Schlagwörter:Carbon nanofiber; Coating; Fretting; Roughness; Solid lubrication
DOI:10.1016/j.surfcoat.2013.03.011
ISSN:0257-8972
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:13.04.2015
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.