A unique direct electrodeposition technique involving very high current densities, high voltages and high electrolyte concentrations is applied for highly selective mass synthesis of stable, isolable, surfactant-free, single-crystalline Bi hexagons on a Cu wire at room temperature. A formation mechanism of the hexagons is proposed. The morphology, phase purity, and crystallinity of the material are well characterized by FESEM, AFM, TEM, SAED, EDX, XRD, and Raman spectroscopy. The thermal stability of the material under intense electron beam and intense laser light irradiation is studied. The chemical stability of elemental Bi in nitric acid shows different dissolution rates for different morphologies. This effect enables a second way for the selective fabrication of Bi hexagons. Bi hexagons can be oxidized exclusively to α-Bi2O3 hexagons. The Bi hexagons are found to be promising for thermoelectric applications. They are also catalytically active, inducing the reduction of 4-nitrophenol to 4-aminophenol. This electrodeposition methodology has also been demonstrated to be applicable for synthesis of bismuth-based bimetallic hybrid composites for advanced applications.
We report on the formation of silver subsurface ion-exchanged metal oxide (silver SIMO) glasses and their surface-enhanced Raman scattering (SERS) activity. The samples were prepared by a combined thermal and chemical three-step methodology and characterized by transmission electron microscopy (TEM), atomic force microscopy (AFM), environmental electron scanning microscopy (ESEM), and UV/Vis spectroscopy. This unique method provides SERS substrates with protection against contamination and strong, reliable and reproducible SERS enhancement. The Raman enhancement factors of the long-term stable SIMO glasses were estimated to approximately 107.
A systematic crystal morphology study on the pharmaceutical model compound caffeine has been conducted on different surfaces: silicon, silver, soda lime glass, and silver subsurface ion-exchanged soda-lime silicate (SIMO) glasses. The morphology of the solid caffeine deposits has been investigated using environmental scanning electron microscopy (ESEM), atomic force microscopy (AFM), and X-ray diffraction (XRD). Needle-shaped caffeine crystals have been observed by drop-casting and also by applying the rapid expansion of supercritical solutions (RESS) technique using supercritical carbon dioxide. The aspect ratio of the crystalline needles typically vary between 10 and 100, but have been observed as large as 500. The XRD data of the RESS products indicate unambiguously the presence of the thermodynamically most stable polymorph of caffeine known as the β-form. Under defined conditions we observe a unique, surface-mediated morphology for caffeine crystals with nearly perfect hexagonal shape. The relative fraction of the hexagons was seen to strongly increase especially when SIMO glasses were used. These hexagons have a distinct upper size limit depending on the solvent and substrate being used. The size distribution analysis of the hexagons yielded an average perimeter of typically 10 µm. The mechanism of the formation process of this new hexagonal motif is explained in terms of the spinodal dewetting of the thin film of caffeine solution on the surface.