The CCQM-K123 key comparison was organized by the Inorganic Analysis Working Group (IAWG) of CCQM to assess and document the capabilities of the national metrology institutes (NMIs) or the designated institutes (DIs) to measure the mass fractions of sodium, calcium, potassium, magnesium phosphorous and sulfur in biodiesel fuel (BDF). The National Metrology Institute of Japan (NMIJ) and National Institute of Standards and Technology (NIST) acted as the coordinating laboratories.
Results were submitted by 11 NMIs and DIs. The participants used different measurement methods, though most of them used inductively coupled plasma-mass spectrometry (ICP-MS), isotope dilution technique with ICP-MS and inductively coupled plasma-optical emission spectrometry (ICP-OES) with microwave acid digestion.
The material was quite challenging and a number of questions were raised at the IAWG meeting. Concerning S, the variation in S results between participants, particularly those using IDMS methods was discussed at the IAWG meeting. BAM, NIST and NMIJ reviewed their experimental conditions, results and/or uncertainty calculations for IDMS. According to the additional evaluation and investigation, the variances between the revised results became smaller than the original one, the revised results were overlapping between IDMS measurements of S content at the k=2 level. It is not possible to calculate a KCRV with values being modified after submission. It was concluded that this KC does not support S measurements.
Accounting for relative expanded uncertainty, comparability of measurement results for each of Na, Ca, K, Mg and P was successfully demonstrated by the participating NMIs or DIs. It is expected that sodium, calcium, potassium, magnesium and phosphorus at mass fractions greater than approximately 0.1 mg/kg, 0.1 mg/kg, 0.05 mg/kg, 0.05 mg/kg and 0.1 mg/kg respectively in biodiesel fuel and similar matrices (fuels and oils etc.) can be determined by each participant using the same technique(s) employed for this key comparison to achieve similar uncertainties mentioned in the present report. Furthermore, the results of this key comparison can be utilized along with the IAWG core capability approach.
Three polyethylene (PE) types with different branching structures were subjected to air, water and ethanol aerosol-assisted dielectric barrier discharges (DBD) for surface modification. Using the air DBD the incorporated oxygen concentration was found to be independent on the branching of PE in contrast to the introduction of OH groups, which was PE-2 > PE-1 > PE-3. For water-aerosol DBD the succession of OH concentration was in the order of PE-1 > PE-2 > PE-3. Ethanol aerosol-assisted DBD produced the lowest concentration of OH groups also independent on the branching of PE. The chemical nature of introduced oxygen functional groups was inspected by X-ray photoelectron spectroscopy (XPS) and assigned as C–O, >C=O/CHO/O–C–O and O=C–O.
A convenient way to overcome the chemical inertness of polyolefin surfaces is to expose them to the atmospheric air plasma of a dielectric barrier discharge (DBD). To improve the efficiency in formation of polar groups at the polyolefin surface, different liquids such as water and ethanol were sprayed as aerosol into the plasma zone between the powered electrode and the polyolefin surface. Both sprayed liquids as well as the polyolefin surface were simultaneously activated; thus, the formation of different functional groups at the polyolefin surface was realized. The type of aerosol-sprayed additive, exposure time, power etc. have been found to determine the efficiency with respect to introduction of polar groups.
Response of linear, branched or crosslinked polyethylene structures on the attack of oxygen plasma
(2014)
Linear, branched and crosslinked polyethylenes (PE) were exposed to the low-pressure oxygen plasma for 2–120 s. In the following the samples were washed with solvents to remove low-molecular weight oxidized material and to excavate the subjacent polymer structure for microscopic characterization. X-ray photoelectron spectroscopy (XPS) measurements provided information about changes in elemental composition and chemical structure of PE after plasma exposure and washing. The calculation of the concentration of tertiary C atoms using XPS data was a measure of branches and crosslinking in the polymer before and after exposure to oxygen plasma. Linear PE was most sensitive towards oxygen plasma and showed the highest concentration in tertiary C atoms after plasma exposure. On the other hand branched PE types, which possess originally more tertiary carbon atoms, have lost two-third of them after 2 s oxygen plasma exposure. Branched PE show also topological changes at their surface as detected by atomic force microscopy. Differential scanning calorimetry measurements confirmed strong changes in crystallinity and molecular orientation of linear PE already after 120 s exposure to the oxygen plasma interpreted as amorphization. These effects should be interpreted as result of crosslinking caused by the recombination of dangling bond sites.