Eingeladener Vortrag
- nein (1)
The present work shows results on elemental distribution analyses in Cu(In,Ga)Se2 thin films for solar cells performed by use of wavelength-dispersive and energy-dispersive X-ray spectrometry (EDX) in a scanning electron microscope, EDX in a transmission electron microscope, X-ray photoelectron, angle-dependent soft X-ray emission, secondary ion-mass (SIMS), time-of-flight SIMS, sputtered neutral mass, glow-discharge optical emission and glow-discharge mass, Auger electron, and Rutherford backscattering spectrometry, by use of scanning Auger electron microscopy, Raman depth profiling, and Raman mapping, as well as by use of elastic recoil detection analysis, grazing-incidence X-ray and electron backscatter diffraction, and grazing-incidence X-ray fluorescence analysis. The Cu(In,Ga)Se2 thin films used for the present comparison were produced during the same identical deposition run and exhibit thicknesses of about 2 µm. The analysis techniques were compared with respect to their spatial and depth resolutions, measuring speeds, availabilities, and detection limits.
The Spray Ion Layer Gas Reaction (Spray-ILGAR) technique is a new variation on the ILGAR technique used to prepare chalcogenide thin films. High quality indium sulfide thin films were produced by Spray-ILGAR with an indirect bandgap of 2.2 eV and a high suitability for use as buffer layers in chalcopyrite solar cells. The process involves the cyclical spray deposition of an indium containing precursor layer followed by its conversion to sulfide using hydrogen sulfide gas. Analysis of the deposition reveals that the indium chloride based precursor is transported via the vapour phase from the spray droplets to the substrate surface.
The surface structure, in particular the surface roughness, and the surface chemistry of titanium implants influence their anchoring in bone. The aim of this study was to analyse metal-bone contact (MBC) after modification of the implant surface, using different materials for blasting. The surface modification of titanium was produced by blasting it with particles made of Al2O3 or bioceramics. The biological effects were then investigated experimentally using 27 rabbits, analysed after 7, 28 and 84 days after the implantation of titanium cylinders treated accordingly. The MBC showed a tendency for more bone after bioceramics were used as a blasting material, compared to Al2O3.