The microstructure and the distribution of chemical elements in laser-welded joints of Al – Mg – Si alloy 6005-T6 are studied. Segregations of chemical elements are detected over grain boundaries in the heat-affected zones of the welded joints. The joints fracture by the intergrain mechanism. A Gleeble 3800 device is used to determine the temperature dependences of the mechanical properties of the alloy with allowance for the special features of the welding cycle. Amethod for evaluating the sensitivity of welded joints of aluminum alloys to formation of liquation cracks with allowance for the local properties of the metal, the welding conditions, and the rigidity of the construction is suggested.
The properties of the welded joints of 6082-T6 alloy produced by friction stir welding (FSW) and laser welding(LW) were studied. The maximum temperature and microhardness fields in the friction stir-welded joints were shown to be asymmetrical. The concentrated energy input during laser welding yields a narrow heat-affected zone (HAZ) with sharp changes in mechanical properties. The strength of the FSW joint constitutes 72% and that of the LWjoint—67% of the base metal strength. In case of LW, the minimum hardness of the joint corresponds to the metal of the welded joint, while in case of FSW, it corresponds to the heat-affected zone. At the same maximum heating temperature, the hardness of the heat-affected zone of the friction stir-welded joint is lower compared to laser welding due to substantially lower rates of heating and cooling.
Welded joints of aluminum alloy 6082-T6 formed by the method of impulse friction stir welding are studied. The effect of the power and frequency of the pulses on the microstructure and mechanical properties of the welded joints is determined. Application of an additional pulse during the welding affects the surface quality and the shape of the weld, the distribution of the oxide layer and of particles of the hardening phase, and the grain size in the zone of dynamic recrystallization.
Welded joints of aluminum alloy 6082-T6 formed by the method of pulse friction stir welding are studied. The effect of the power and frequency of the pulses on the microstructure and mechanical properties of the welded joints is determined. Application of an additional pulse during the welding affects the surface quality and the shape of the weld, the distribution of the oxide layer and of particles of the hardening phase, and the grain size in the zone of dynamic recrystallization.