AlGaN/GaN heterostructure field effect transistors (HFETs) were irradiated with 2 MeV protons, carbon, oxygen, iron and krypton ions with fluences ranging from 1 × 109 cm−2 to 1 × 1013 cm−2. DC, pulsed I–V characteristics, loadpull and S-parameters of the AlGaN HFET devices were measured before and after irradiation. In parallel, a thick GaN reference layer was also irradiated with the same ions and was characterized by X-ray diffraction, photoluminescence, Hall measurements before and after irradiation. Small changes in the device performance were observed after irradiation with carbon and oxygen at a fluence of 5 × 1010 cm−2. Remarkable changes in device characteristics were seen at a fluence of 1 × 1012 cm−2 for carbon, oxygen, iron and krypton irradiation. Similarly, remarkable changes were also observed in the GaN layer for irradiations with fluence of 1 × 1012 cm−2. The results found on devices and on the GaN layer were compared and correlated.
AlGaN/GaN heterostructure field effect transistors (HFETs) were irradiated with protons as well as carbon, oxygen, iron and krypton ions of high (68 and 120 MeV) and low (2 MeV) energy with fluences in the range from 1x107 to 1x1013 cm-2. High energy irradiation with protons, carbon and oxygen produced no degradation in devices while krypton irradiation at the fluence of 1x1010 cm-2 resulted in a small reduction of 2% in the transconductance. Similarly, for GaN samples irradiated with protons, carbon and oxygen at high energy no changes were seen by XRD, PL and Hall effect, while changes in lattice constant and a reduction in PL intensity were observed after irradiation with high energy krypton. Low energy irradiation with carbon and oxygen at a fluence of 5x1010 cm-2 results in small change in the device performance while remarkable changes in device characteristics are seen at a fluence of 1x1012 cm-2 for carbon, oxygen, iron and krypton irradiation. Similarly changes are also observed by XRD, PL and Hall effect for the thick GaN layer irradiated at the fluence of 1x1012 cm-2. The device results and GaN layer properties are strongly correlated.
The effect of proton, carbon, oxygen and krypton irradiation on AlGaN HFET devices has been studied. Irradiation was performed at 68 and 120 MeV with fluences in the range from 1 × 10^7 to 1 × 10^13 cm2 . Before and after irradiation, dc and pulsed I – V characteristics, loadpull and S -parameters of the AlGaN HFET devices were measured. A thick GaN reference layer was characterized by x-ray diffraction, photoluminescence and Hall measurements before and after irradiation. Proton, carbon and oxygen irradiation show no degradation in devices while krypton irradiation shows a small change at a fluence of 1 × 10 10 cm2 in the device characteristics. The device results are correlated with the thick GaN results.
The Fraunhofer Institute for Photonic Microsystems (Fraunhofer IPMS) develops spatial light modulators (SLMs) based on arrays of tiltable micro mirrors on a semiconductor chip. Typical applications are pattern generation for deepUV-laser mask writing or structured illumination in microscopy. Development and optimization of such SLMs requires detailed knowledge of the device behaviour under operating conditions. Here, the flatness of each single mirror effects the image resolution and contrast of the generated pattern and is amongst others a characteristic property of SLMs. In this context a surface topography measurement under laser exposure (in situ) was designed. The interferometric setup uses the phase-shift principle and allows a resolution in z-direction in the single-digit nanometer range. During irradiation with UV-laser light at 248 nm (KrF) and energy densities of up to 20 mJ/cm2 the change in single micro-mirrors topography was detected in situ. Measurementswith varying pulse energies
were carried out to identify an impacton the device
performance. In general, the setup is neither limited to a
specific illumination wavelength nor to micro-mirrors as structures under test.
Due to the unique electronic structures, graphene and other 2D Materials are considered as materials which can enable and extend the functionalities and performance in a large variety of applications, among them in microelectronics. At this point, the investigation and preparation of graphene devices in conditions resembling as close as possible the Si technology environment is of highest importance.Towards these goals, this paper focuses on the full spectra of graphene research aspects in 200mm pilot line. We investigated different process module developments such as CMOS compatible growth of high quality graphene on germanium and its growth mechanisms, transfer related challenges on target substrates, patterning, passivation and various concepts of contacting of graphene on a full 200 mm wafers. Finally, we fabricated proof-of-concept test structures e.g. TLM, Hall bars and capacitor structures to prove the feasibility of graphene processing in the pilot line of IHP.