Keywords
- TNB-V4 (1)
- TiAl (1)
- Titanium Aluminides (1)
- hot die forging (1)
Institute
In the cast condition g titanium aluminide alloys that solidify completely through the b phase are
characterized by fine and homogeneous microstructures, weak textures and low segregation. For these reasons such alloys have a relatively good workability and can be closed-die forged without preceding ingot breakdown even if the alloys contain no large fractions of the b phase at the working temperature. The present work was devoted to a combined study of the constitution and microstructural morphologies that develop in various two-step heat treatments of a single-step forged b solidifying alloy. The
study included high-energy X-ray diffraction for in situ investigations of the constitution at the heat treatment temperature. It was observed that the phase ransformations are quite sluggish in the material which results in fine microstructures and some conditions that significantly deviate from thermodynamic equilibrium. Further, tensile and creep testing was carried out on the different material conditions in order to identify the range in which the properties can be varied. It is found that this easily forgeable material exhibits comparable strength, ductility and creep strength as more conventional peritectically solidifying alloys.
Recent research on Co-based and CoNi-based alloys revealed that the Co–Al–W-system provides interesting properties, however, the high content of W addition triggers high mass density of alloys which limits its industrial application. Therefore, new high temperature superalloys based on the Co–Ni–Al–Ti-system with high content Cr and strengthened by γ′-(Ni,Co)3(Cr,Al,Ti) precipitates, have been developed, and the effect of different refractory element additions was investigated. STEM-EDS and HEXRD were employed to determine the elemental partitioning behavior and the lattice misfit between the γ and γ′ phases. Ta and Nb strongly concentrate within the γ′ phase, whereas Mo weakly partitions to the γ phase. W distributes equally between the γ and γ′ phases. These new superalloys have an unexpectedly high positive misfit compared with some conventional Ni-based superalloys and Co-based superalloys. Nb and Ta additions increase the lattice misfit further, while Mo and W decrease the lattice misfit. The effect of refractory elements alloying on the yield stress at room temperature was evaluated by analyzing the contributions of different strengthening mechanisms. Alloying with Nb or Ta significantly improves precipitation strengthening by increasing the antiphase boundary energy. Mo has the highest solid solution strengthening effect in the γ phase, followed by W. Compared with some conventional Ni-based superalloys, the investigated new CoNi-based superalloys exhibited better mechanical properties at high temperature, which indicates that these compositionally complex alloys are possible candidates for high temperature applications.
Microstructure development and hardness of a powder metallurgical multi phase gamma-TiAl based alloy
(2012)