In special cases of angle beam ultrasonic measurement – e.g. defect detection in hot solids as well as flow measurement of liquid gases or energy storage mediums [1] – the applied transducer has to withstand extreme temperatures. Since the irradiation angle into the specific material is determined not only by wedge design, but also by the speed of sound in both the wedge material and the tested object, the developer must take into account the speed of the wave propagation in a wedge material over the whole temperature range of transducers application.
In this study we investigate the temperature dependence of the speed of longitudinal wave propagation in 10 different materials in the range from -200 °C to 400 °C. The investigated materials belong to different material classes (ceramics, glass, as well as ferrous and non-ferrous metals) and are all temperature-resistant up to at least 600 °C, and therefore applicable as wedge materials in an ultrasonic transducer for use at extreme temperatures.
The objective of this work is to investigate the strain localization
and slip activation of the microstructure of oligo-crystalline 316LVM steel struts evolving during different cyclic bending deformation stages (number of cycles) and loading conditions (maximum stress and neutral). A micro-scale three-point bending fixture was designed and incorporated into a micro tensile/compression machine inside a scanning electron microscope (SEM) to perform in-situ electron backscatter diffraction (EBSD) measurements during different phases of cyclic fatigue testing. The following results were obtained:
1) The quantitative strain could be compared after each stage of
deformation.
2) The rotation of the grains orientations is observed during the cyclic deformation while the morphology did not change significantly. The results contribute to the understanding of the evolution of the microstructure at low strain variations under bending fatigue conditions, and can support the prediction of the fatigue life of 316LVM stainless steel oligocrystalline microdevices like coronary artery stents.