Refine
Document Type
- Article (3)
Language
- English (3)
Is part of the Bibliography
- no (3)
Keywords
- additive manufacturing (AM) (1)
- dimensional accuracy (1)
- filament color (1)
- fused deposition modeling (FDM) (1)
- fused deposition modeling (FDM); fused filament fabrication (FFF); polylactic acid (PLA); layer height; layer thickness; filament color; PLA color; dimensional accuracy; tensile strength (1)
- fused deposition modeling (FDM); polylactic acid (PLA); printing scenario; filament color; dimensional accuracy; tensile strength (UTS) (1)
- fused filament fabrication (FFF) (1)
- polylactic acid (PLA) (1)
- printing speed (1)
- ultimate tensile strength (UTS) (1)
Institute
This study examines the effect of elevated printing speeds (100–600 mm/s) on the dimensional accuracy and tensile strength of PLA components fabricated via fused deposition modeling (FDM). To isolate the influence of printing speed, all other parameters were kept constant, and two filament variants—natural (unpigmented) and black PLA—were analyzed. ISO 527-2 type 1A specimens were produced and tested for dimensional deviations and ultimate tensile strength (UTS). The results indicate that printing speed has a marked impact on both geometric precision and mechanical performance. The optimal speed of 300 mm/s provided the best compromise between dimensional accuracy and tensile strength for both filaments. At speeds below 300 mm/s, under-extrusion caused weak layer bonding and air gaps, while speeds above 300 mm/s led to over-extrusion and structural defects due to thermal stress and rapid cooling. Black PLA yielded better dimensional accuracy at higher speeds, with cross-sectional deviations between 2.76% and 5.33%, while natural PLA showed larger deviations of up to 8.63%. However, natural PLA exhibited superior tensile strength, reaching up to 46.59 MPa, with black PLA showing up to 13.16% lower UTS values. The findings emphasize the importance of speed tuning and material selection for achieving high-quality, reliable, and efficient FDM prints.
Dimensional accuracy and mechanical properties of components printed by fused deposition modeling (FDM) are influenced by several process parameters. In this paper, the authors targeted the effect of the printing scenario and the PLA (polylactic acid) color on parts’ quality. Three scenarios were analyzed: individually printing, simultaneously printing of three, respective five specimens of natural (transparent), red, grey, and black PLA. The temperature variations of successive deposited layers were recorded for the black PLA. The dimensional accuracy of tensile specimens was evaluated, tensile tests were performed, and the results were correlated with the mesostructure of the prints. The effect of the independent variables on the measured parameters was analyzed by ANOVA. The experiments revealed differences for the same printing scenario regarding cross-section area (up to 5.71%) and tensile strength (up to 10.45%) determined by the material color. The number of specimens printed simultaneously and the position of the pecimens on the build plate were found to influence too, but less than the color. Thus, increasing from one to five the number of specimens printed at a time altered both the dimensional accuracy (up to 3.93% increase of the cross-section area) and the tensile strength (up to 3.63% reduction).
Among the FDM process variables, one of the less addressed in previous research is the filament color. Moreover, if not explicitly targeted, the filament color is usually not even mentioned.
Aiming to point out if, and to what extent, the color of the PLA filaments influences the dimensional precision and the mechanical strength of FDM prints, the authors of the present research carried out experiments on tensile specimens. The variable parameters were the layer height (0.05 mm, 0.10 mm, 0.15 mm, 0.20 mm) and the material color (natural, black, red, grey). The experimental results clearly showed that the filament color is an influential factor for the dimensional accuracy as well as for the tensile strength of the FDM printed PLA parts. Moreover, the two way ANOVA test performed revealed that the strongest effect on the tensile strength was exerted by the PLA color (2 = 97.3%), followed by the layer height (2 = 85.5%) and the interaction between the PLA color and the layer height (2 = 80.0%). Under the same printing conditions, the best dimensional accuracy was ensured by the black PLA (0.17% width deviations, respectively 5.48% height deviations), whilst the grey PLA showed the highest ultimate tensile strength values (between 57.10 MPa and 59.82 MPa).