Refine
Document Type
- Article (4)
Language
- English (4)
Is part of the Bibliography
- no (4)
Keywords
- 316L stainless steel (1)
- abrasion (1)
- additive manufacturing (1)
- batch hot-dip galvanizing (1)
- brazing tapes (1)
- coating (1)
- corrosion behavior (1)
- corrosion protection (1)
- deposition strategy (1)
- directed energy deposition-arc (1)
In recent decades, batch hot-dip galvanized (HDG) steel has proven itself in practical applications due to the good corrosion resistance of its components. Despite the importance of the mechanical-load-bearing capacity of these coatings, the wear behavior has, so far, only been investigated very sporadically and not systematically, so a quantification of the wear behavior and statements on the mechanisms are vague. Therefore, two body wear tests with bonded abrasive grain were carried out. Varying the friction rolls, load, and total number of cycles, the wear behavior was investigated. The mass loss and the layer thickness reduction were measured at different intervals. After the test, the microstructure in the cross- section and the hardness according to Vickers (0.01 HV) were evaluated. The results showed that the wear behavior of HDG coatings against abrasive loads can be characterized with the selected test conditions. Initially, the applied load removed the soft η-phase. As the total number of cycles increases, the η- and ζ-phases deform plastically, resulting in a lower mass reduction compared to that expected from the measured layer thickness. The characteristic structure of a batch HDG coating with hard intermetallic Zn-Fe phases and an outer pure zinc phase has demonstrated effective resistance to abrasion.
Directed Energy Deposition-Laser (DED-L) enables high-performance coatings through melting and successive powder deposition. Its compositional flexibility suits functionally graded layers that enhance corrosion and wear resistance. This study aimed to improve parameters for producing dense, defect-free, graded Ni- and Fe-based coatings by varying the scanning speed and deposition strategy (monodirectional versus bidirectional, with/without layer rotation), while keeping the power and hatch distance constant. Laser and electron microscopy were used to link parameters to porosity and uniformity. Optimal settings minimized pores, improved interlayer bonding and preserved geometry; inadequate parameters yielded porous, irregular deposits. A bidirectional path with 90° rotation appeared best. Ongoing research activities are needed to assess its properties.
Highlights
What are the main findings?
- Bidirectional samples show fewer pores than samples with monodirectional movement.
- Increasing the scanning speed leads to lower porosity (bidirectional scanning mode with 90°
layer rotation).
- Bidirectional deposition with 90° layer rotation exhibits best quality
What are the implications of the main findings?
- Systematic study of scanning speed and deposition strategy.
- Practical guidance for process improvement of graded metal coatings; properties under evaluation.
- Functionally graded Ni-Fe coatings fabricated by DED-L with tailored microstructures.
Among all additive manufacturing processes, Directed Energy Deposition-Arc (DED-Arc) shows significantly shorter production times and is particularly suitable for large-volume components of simple to medium complexity. To exploit the full potential of this process, the microstructural, mechanical and corrosion behavior have to be studied. High stickout distances lead to a large offset, which leads to an instable electric arc and thus defects such as lack of fusion. Since corrosion preferentially occurs at such defects, the main objective of this work is to investigate the influence of the stickout distance on the corrosion
behavior and microstructure of stainless steel manufactured by DED-Arc.
Within the heterogenous structure of the manufactured samples lack of fusion defects were detected. The quantity of such defects was reduced by applying a shorter stickout distance. The corrosion behavior of the additively manufactured specimens was investigated by means of potentiodynamic polarization measurements. The semi-logarithmic current density potential curves showed a similar course and thus similar corrosion resistance like that of the conventionally forged sample. The polarization curve of the reference material shows numerous current peaks, both in the anodic and cathodic regions. This metastable behavior is induced by the presence of manganese sulfides. On the sample surface a local attack by pitting corrosion was identified.
Traditionally, repairing coated substrates requires completely removing damaged, wear-resistant layers before recoating. This process leads to high costs, extended downtime, and material waste. Flexible brazing tapes, which are composed of alloy powder and an organic binder, offer an alternative to full coating removal for targeted repairs. Despite this, the process of vacuum brazing these tapes may lead to the formation of defects, including pores caused by trapped gases or residual binder, which compromise coating durability and corrosion resistance. This study focuses on the utilization of laser remelting as a method for post-processing nickel- and iron-based mixed alloy brazing tapes, with the aim of improving the integrity of the coating. Surface quality was assessed via microscopy and microhardness testing by systematically varying laser power, scanning speed, and hatch distance. Among the parameters studied, the most suitable laser parameter combination was found to be 350 W laser power, 250 mm/s scanning speed, and a hatch distance of 0.02 mm. These parameters yielded crack- and pore-free coatings with a remelting depth of 160.3 ± 17.2 µm and a microhardness of 701 ± 23 HV1, which is an 85% increase over as-brazed samples. Wear testing revealed a reduced coefficient of friction, and electrochemical corrosion tests showed lower corrosion current density and enhanced repassivation behavior in remelted coatings. These improvements demonstrate that laser remelting significantly enhances the microstructure, hardness, wear resistance, and corrosion performance of brazed coatings, providing an effective method for localized repair while minimizing material consumption and processing duration.