Reproducible Superinsulation Materials: Organosilica-Based Hybrid Aerogels with Flexibility Control
(2024)
In this study, we report highly crosslinked hybrid aerogels with an organic backbone based on vinylmethyldimethoxysilane (VMDMS) with tuneable properties. For an improved and highly reproducible synthesis, a prepolymer based on 2,4,6,8-tetramethyl-2,4,6,8-tetravinylcyclotetrasiloxane (D4V4) and VMDMS as monomers was prepared and purified. Di-tert-butylperoxide (DTBP) concentrations of 1 mol% initiate the radical polymerization of the mentioned monomers to achieve high yields of polymers. After purification, the obtained viscous polyorganosilane precursor could be reproducibly crosslinked with dimethyldimethoxysilane (DMDMS) or methyltrimethoxysilane (MTMS) to form gels in benzylic alcohol (BzOH), water (H2O) and tetramethylammonium hydroxide (TMAOH). Whereas freeze-drying these silica-based hybrid aerogels led to high thermal conductivity (>20 mW m−1K−1) and very fragile materials, useful aerogels were obtained via solvent exchange and supercritical drying with CO2. The DMDMS-based aerogels exhibit enhanced compressibility (31% at 7 kPa) and low thermal conductivity (16.5 mW m−1K−1) with densities around (0.111 g cm−3). The use of MTMS results in aerogels with lower compressibility (21% at 7 kPa) and higher density (0.124 g cm−3) but excellent insulating properties (14.8 mW m−1K−1).
The synergistic combination of various sorbitol-based organogelators with polyolefins allows the preparation of porous support structures for immobilized phase change materials (PCMs). Using a PCM as a solvent for the preparation leads to dimensionally stable composite materials with extremely high loading rates and low leakage of PCMs. Detailed investigations were performed on the kind of polyolefin support and its mass fraction concentration in the PCM, the temperature-dependent softening and failure under superimposed load, the efficiency of heat transport and the retention capacity over several melting/solidification cycles in various measurement setups. In particular, paraffin wax in combination with 1,2,3-trideoxy-4,6:5,7-bis-O-[(4-propylphenyl)methylene]-nonitol (TBPMN) and ultrahigh molecular weight polyethylene (UHMWPE) showed the best results in terms of high dimensional stability, low leakage, excellent processability and competitive heat capacity. The herein-established one-step preparation method saves time and energy compared to the loading of pre-formed porous supports and improves application-related properties at the same time.
Abstract
Electrospinning has been widely used as a versatile technique to generate nanofibers of various materials. It is also helpful in teaching topics ranging from macromolecular chemistry to physics, safety, and sustainability at various levels of difficulty and student involvement. Simple and safe hands-on experiments/manual assays can be realized for less than 30 euros to demonstrate polymer viscosity and nanofiber alignment and solubility. Students can further study (super)hydrophobicity and even upcycle packaging waste into useful filter materials but also improve the electrospinning setup from a manual assay to an inexpensive Arduino-based 3D printed research platform. Alternatively, the latter can be used for teacher demonstrations of more challenging experiments that can also be easily done using a commercial syringe-pump.