New Polyurethanes with a polyurea matrix

  • Based on a previously published (Peshkov 2011) synthesis route of nanoscale oligourea dispersion polyols (NODP) a new type of polyurethanes with a polyurea matrix was developed. Polyurethanes with high hardness and elasticity were prepared by reacting a formulation based on the NODP’s and di- or polyisocyanates. The polyurethanes obtained as films were characterised by mechanical tests and dynamic mechanical analysis (DMA). The phase structure depends on the amount of nanoparticles present, the isocyanate index, and the mode of curing. It is suggested that nanoparticles have to be of similar size as the matrix into which they are embedded to show a typical nano- effect such as shown here. These elastic polymers show an unusual high Shore D hardness of some 70 and tensile strength up to 47 MPa at elongations at break of 7 %.
  • Basierend auf einem bereits veröffentlichten Syntheseweg (Peshkov 2011) für nanoskalige Harnstoff Dispersions Polyole (PHD) wurde ein neuer Typ von Polyurethanen mit einer Polyharnstoff Matrix entwickelt. Durch Umsetzung der PHD’s mit Di- bzw. Polyisocyanaten wurden elastische Polyurethane mit hoher Härte erhalten. Die als Film präparierten Polyurethane wurden durch Zugprüfung und Dynamisch Mechanische Analyse (DMA) charakterisiert. Die Phasenstruktur ist abhängig von der Menge an Nanopartikeln, dem Isocyanatindex und dem Härtungsregime. Die Ergebnisse deuten daraufhin, dass die Nanopartikel, um einen typischen Nano-Effekt zu zeigen, von ähnlicher Größe sein müssen wie die Matrix, in die sie eingebettet sind. Die erhaltenen elastischen Polymere zeigen ungewöhnlich hohe Shore-D-Härten im Bereich von 70 und Zugfestigkeiten bis zu 47 MPa bzw. Bruchdehnungen von 7 %.

Download full text files

Export metadata

Additional Services

Search Google Scholar Statistics
Metadaten
Author:Vladimir Peshkov, Gerhard Behrendt, Rozeta Evtimova, Michael HerzogORCiD
URN:urn:nbn:de:kobv:526-opus-1259
DOI:https://doi.org/10.15771/0949-8214_2012_1_12
ISSN:0949-8214
Parent Title (German):Wissenschaftliche Beiträge 2012
Document Type:Article in a Periodical of the TH Wildau
Language:English
Year of Publication:2012
Year of first Publication:2012
Publishing Institution:Technische Hochschule Wildau
Release Date:2012/01/20
Volume:16
First Page:93
Last Page:102
Faculties an central facilities:Fachbereich Ingenieurwesen / Wirtschaftsingenieurwesen (bis 8/2014)
Dewey Decimal Classification:6 Technik, Medizin, angewandte Wissenschaften / 62 Ingenieurwissenschaften / 620 Ingenieurwissenschaften und zugeordnete Tätigkeiten
TH Wildau publications:Wissenschaftliche Beiträge
Licence (German):Creative Commons - CC BY-NC-ND 3.0 DE - Namensnennung - Nicht-kommerziell - Keine Bearbeitung 3.0 Deutschland
Verstanden ✔
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.