Effect of the loop forming process on the lifetime of aluminum heavy wire bonds under accelerated mechanical testing

  • Heavy wire bonding is one of the most common interconnection technologies in manufacturing of high-power electronics. For industrial applications, the long-term reliability of these connections is crucial. Besides the selection of the wire material and the loop geometry itself, the loop forming process parameters also have an influence on the reliability of the wire bond. In this work, the influence of the backward bond head movement during wire bonding process on the quality of wire bond connections was systematically investigated and qualified by cyclic mechanical lifetime tests, surface roughness measurements of the heel area by laser confocal microscopy and static pull tests. The wire bond loops were fabricated with 300 μm aluminum H11 and H14CR wires with different hardness values. The lifetime at low frequency cycle and high frequency cycle regime was determined by means of two different mechanical cyclic test methods operating at 5 Hz and at 60 kHz respectively. The results have shown, that the surface topology of the heel region caused by the initial plastic deformation during the loop forming process has a significant effect on the wire bond failure due to heel cracking. The number of loading cycles to failure shows an inverse correlation with the degree of surface roughness in a so called wrinkling analysis in the low and high frequency cycle regime. The soft wire exhibits different lifetimes compared to the hard ones depending on the testing conditions, while a significant decrease of the lifetime is observed with >30 % reverse movement during bonding in all cases.

Download full text files

Export metadata

Additional Services

Search Google Scholar Statistics
Metadaten
Author:Florens Felke, Anne Groth, Martin HempelORCiD, Bernhard CzernyORCiD, Golta KhatibiORCiD, Torsten Döhler, Ute Geißler
URN:urn:nbn:de:kobv:526-opus4-18631
DOI (Version of Record):https://doi.org/10.1016/j.microrel.2024.115337
Parent Title (English):Microelectronics Reliability
Publisher:Elsevier
Document Type:Article
Language:English
Year of Publication:2024
Publishing Institution:Technische Hochschule Wildau
Release Date:2024/02/22
Tag:aluminum heavy wire bonding; heel crack; loop forming process; mechanical accelerated lifetime testing method; wrinkling
Volume:154
Article Number:115337
Source:Felke, F., Groth, A., Hempel, M., Czerny, B., Khatibi, G., Döhler, T., & Geißler, U. (2024). Effect of the loop forming process on the lifetime of aluminum heavy wire bonds under accelerated mechanical testing. Microelectronics Reliability, 154, 115337. doi:10.1016/j.microrel.2024.115337
Faculties an central facilities:Fachbereich Ingenieur- und Naturwissenschaften
Dewey Decimal Classification:6 Technik, Medizin, angewandte Wissenschaften / 62 Ingenieurwissenschaften / 621 Angewandte Physik
Funding:Projekt DEAL
Licence (German):Creative Commons - CC BY - Namensnennung 4.0 International
Verstanden ✔
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.