TY  - JOUR
U1  - Wissenschaftlicher Artikel
A1  - Herz, Jonas
A1  - Muscat, Dirk
A1  - Strübbe, Nicole
T1  - The Influence of Fillers on the Reinforcement Capabilities of Polypropylene Based Mono-Material and Core-Shell Fibers in Concrete, a Comparison
JF  - Polymers
N2  - Noncorrosive concrete reinforcement, such as polymer fibers, is needed to overcome the current issues caused by corroded steel reinforcements. Fibers made of polypropylene show a low bonding behavior in concrete. Fillers can help to overcome this issue but often lead to reduced mechanical properties. Core-shell fibers, which split the mechanical properties and the bonding behavior between the core and the shell component, could be a solution. This study investigates mono-material and core-shell fibers produced with calcium carbonate and bentonite fillers and compares their behavior in tensile tests, density measurements, contact angle measurements, topography measurements, single fiber pull-out tests, reflected light microscopy, and thermogravimetric analysis. The fillers caused an increased drawability, resulting in higher mechanical properties. Further, in the core-shell fibers, the calcium carbonate increased the surface roughness, which led to a better anchoring of the fiber in concrete, which was also visible in the deformation during pull-out observed in reflected light microscopy pictures. The thermogravimetric analysis showed a delay in onset of degradation for fibers containing bentonite.
AB  - Noncorrosive concrete reinforcement, such as polymer fibers, is needed to overcome the current issues caused by corroded steel reinforcements. Fibers made of polypropylene show a low bonding behavior in concrete. Fillers can help to overcome this issue but often lead to reduced mechanical properties. Core-shell fibers, which split the mechanical properties and the bonding behavior between the core and the shell component, could be a solution. This study investigates mono-material and core-shell fibers produced with calcium carbonate and bentonite fillers and compares their behavior in tensile tests, density measurements, contact angle measurements, topography measurements, single fiber pull-out tests, reflected light microscopy, and thermogravimetric analysis. The fillers caused an increased drawability, resulting in higher mechanical properties. Further, in the core-shell fibers, the calcium carbonate increased the surface roughness, which led to a better anchoring of the fiber in concrete, which was also visible in the deformation during pull-out observed in reflected light microscopy pictures. The thermogravimetric analysis showed a delay in onset of degradation for fibers containing bentonite.
KW  - fibers
KW  - extrusion
KW  - coextrusion
KW  - polymer drawing
KW  - polypropylene
KW  - calcium carbonate
KW  - bentonite
KW  - core-shell
KW  - mono-material
KW  - concrete
Y1  - 2025
U6  - https://doi.org/10.3390/polym17131781
DO  - https://doi.org/10.3390/polym17131781
VL  - 17
IS  - 13
SP  - 24
PB  - MDPI
CY  - Basel
ER  -