Labor Biomaterialien
Refine
Year of publication
Language
- English (20)
Has Fulltext
- no (20) (remove)
Is part of the Bibliography
- no (20)
Keywords
- Magnesium (2)
- Adhesives (1)
- Aluminum Silicates (1)
- Bioactivity (1)
- Biodegradable materials (1)
- Biomaterials (1)
- Bond strength (1)
- Ceramics (1)
- Chitosan (1)
- Classification (1)
Institute
- Fakultät Maschinenbau (20) (remove)
Begutachtungsstatus
- peer-reviewed (6)
Mg and Mg alloys are becoming more and more of interest for several applications. In the case of biomaterial applications, a special interest exists due to the fact that a predictable degradation should be given. Various investigations were made to characterize and predict the corrosion behavior in vitro and in vivo. Mostly, the simple oxidation of Mg to Mg2+ ions connected with adequate hydrogen development is assumed, and the negative difference effect (NDE) is attributed to various mechanisms and electrochemical results. The aim of this paper is to compare the different views on the corrosion pathway of Mg or Mg alloys and to present a neglected pathway based on thermodynamic data as a guideline for possible reactions combined with experimental observations of a delay of visible hydrogen evolution during cyclic voltammetry. Various reaction pathways are considered and discussed to explain these results, like the stability of the Mg+ intermediate state, the stability of MgH2 and the role of hydrogen overpotential. Finally, the impact of MgH2 formation is shown as an appropriate base for the prediction of the degradation behavior and calculation of the corrosion rate of Mg and Mg alloys.
Statement of problems: Computer-aided design/computer-assisted machining systems offer the possibility of fabricating restorations from one machinable ceramic block. Whether multishaded blocks improve esthetic results and are a viable alternative to individually stained ceramics has not been fully determined.
Purpose: The aim of this investigation was to examine the effect of multishaded blocks on the esthetic appearance of all-ceramic CEREC crowns and compare these crowns with single-shade and stained restorations.
Material and methods: Ten subjects were included in this study. For each subject, 6 different crowns were milled with the use of a CEREC machine. One crown was milled from each of the following machinable ceramic materials: CEREC Vitablocs Mark II in classic colors; Vitablocs Mark II in 3D-Master colors; Vitablocs Mark II in either classic or 3D-Master colors, with additional staining; Megadenta Bloxx multishaded; Mark II experimental multilayer; and an experimental multilayer leucite ceramic. Three independent examiners assessed the esthetic appearance of crowns fabricated to match each subject's anterior tooth shade. A scale of 1 to 6 was used to score the shade match and esthetic adaptation of each crown, with 1 representing excellent characteristics and 3.5 serving as the threshold for clinical acceptability. The examiners' scores were averaged, and the mean values were analyzed with the Wilcoxon signed rank test (P<or=.05).
Results: Only individually stained Mark II restorations achieved a mean score below the threshold of 3.5 for all 10 subjects. These restorations were significantly more esthetic (P<or=.05) than restorations fabricated from all other materials except the Mark II experimental multilayer ceramic. The second best results were obtained for crowns made from single-shaded Mark II 3D-Master blocks: 6 out of 10 restorations were scored below 3.5. Two of the layered materials (Mark II experimental and Bloxx) followed with 5 acceptable restorations out of 10.
Conclusion: Within the limitations of this study, the results provide no evidence that multicolored machinable ceramics improve the esthetics of all-ceramic crowns.
The bond between methacrylic polymer adhesives and dental restoratives is not perfect and may fail either in the short or in the long term. This study aims to evaluate the effects of particle incorporation in a self-etch model adhesive on mechanical and physical properties that are relevant during application and service. Filled adhesives containing 5, 10, 15 or 25 wt% glass fillers were compared to their unfilled counterpart in terms of water sorption and solubility; viscosity and dynamic viscosity during polymerization were recorded using rheological measurements and compared to FTIR analysis of the real-time degree of cure. Elastic modulus and ultimate tensile strength measurements were performed in uniaxial tension; the energy to fracture was used to calculate the fracture toughness of the adhesives. Finally, the experimental adhesives were applied on dentin substrate to test the bond strength using the microtensile test. Results showed that the incorporation of 5–10 wt% nanofiller to self-etching dental adhesives is efficient in accelerating the polymerization reaction and increasing the degree of cure without compromising the film viscosity for good wettability or water sorption and solubility. Fillers increased the elastic modulus, tensile strength and fracture toughness to a plateau between 5 and 15 wt% filler concentration, and despite the tendency to form agglomerations, active crack pinning/deflection toughening mechanisms have been observed. The bond strength between resin composite and dentin was also improved when adhesives with up to 10 wt% fillers were used, with no additional improvements with further packing. The use of fillers to reinforce dental adhesives may therefore be of great practical benefit by improving curing and mechanical properties.
Operational wear behaviour of 3D-printed lightweight metal gears: EDS and oil analysis comparison
(2024)
Additive manufacturing (AM) has come to the fore in recent years among manufacturing techniques. This technique, which has different advantages than traditional ones such as casting, forging and machining, is expected to be widely used in producing machine parts like gears in the coming years. Therefore, experimental data on AM parameters for lightweight metal gears are important for industrial production. In this study, a wear test was applied to AlSi10Mg and Ti6Al4V gears under operational conditions, and the wear behaviour of conventionally and additively manufactured gears was compared. The amount of abrasion elements was determined by analysing the oil in the gearbox. In addition, gear surfaces were analysed using scanning electron microscopy and an energy-dispersive spectrometer before and after wear. Thus, the wear behaviour of gears produced by conventional and AM under service conditions was demonstrated comparatively.
We investigate the mechanical and microstructural properties of a diamond-like carbon coating (DLC) which is deposited by plasma enhanced chemical vapor deposition (PECVD) onto an alumina/aluminosilicate glass composite used for biomedical applications. Ball-on-ring tests yield a fracture strength that is essentially influenced by the surface topology/roughness. The surface topology of the coating is investigated by atomic force microscopy (AFM). Tribology tests and nanoindentation represent the wear resistance and hardness; these are properties that are mainly influenced by the microstructural properties of the DLC coating. This microstructure is investigated by transmission electron microscopy (TEM) and analyzed by parallel electron energy loss spectroscopy (PEELS). For the general applicability of the coated composite, the interfacial adhesion of the DLC coating on the comparably rough substrate (roughness amplitudes and wavelengths are in the micrometer range) is important. Therefore, we focus on TEM investigations that show the interface to be free of gaps and pores that we, together with a characteristic microstructure adjacent to the interface, relate to the excellent adhesion. The interlayer consists of a high density of SiC grains, part of them directly bound to the substrate, and part of them bound to other SiC grains. This interlayer is followed by an essentially different region of the coating as concerns the microstructure; this region consists of nanocrystalline diamond particles embedded in an amorphous carbon matrix. It is this heterogeneous microstructure to which we attribute (i) the good adhesion based upon the interface stabilizing SiC grains, and (ii) the high hardness and wear resistance based upon the diamond nanocrystals in the coating.
The morphology and microstructure of an Al2O3 glass composite (trade name In-Ceram, Vita Zahnfabrik) were studied using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The composite was produced by infiltration of a lanthanum-based glass throughout a porous Al2O3 body. This alumina body was formed by three classes of particles differing in size and shape: faceted particles typically ≤4 μm in diameter, platelets of average diameter 8 μm, 1.5 μm thickness, and small spheres 0.4 μm in diameter. The outstanding strength properties of the composite (600 MPa, ball-on-ring test) are a result of the high wetting capability of the glass phase on the Al2O3 surface. In addition, plastic strain relaxation in the faceted particles by dislocation formation compensates partially for residual stresses and impedes crack formation at the glass/Al2O3 interface.
Production of a dental reconstruction comprises: (a) forming a mold (12) from a model (10); (b) using (12) to make an isotropically heat-expandable replica from a ceramic precursor (14); (c) oxidizing (14) to produce an enlarged ceramic replica; (d) forming a silicone mold from this replica; (e) using (d) to make a second ceramic replica; and (f) sintering the second replica with volume reduction to form a replica identical to (10).
We investigate the mechanical and microstructural properties of a diamond-like carbon coating (DLC) which is deposited by plasma enhanced chemical vapor deposition (PECVD) onto an alumina/aluminosilicate glass composite used for biomedical applications. Ball-on-ring tests yield a fracture strength that is essentially influenced by the surface topology/roughness. The surface topology of the coating is investigated by atomic force microscopy (AFM). Tribology tests and nanoindentation represent the wear resistance and hardness; these are properties that are mainly influenced by the microstructural properties of the DLC coating. This microstructure is investigated by transmission electron microscopy (TEM) and analyzed by parallel electron energy loss spectroscopy (PEELS). For the general applicability of the coated composite, the interfacial adhesion of the DLC coating on the comparably rough substrate (roughness amplitudes and wavelengths are in the micrometer range) is important. Therefore, we focus on TEM investigations that show the interface to be free of gaps and pores that we, together with a characteristic microstructure adjacent to the interface, relate to the excellent adhesion. The interlayer consists of a high density of SiC grains, part of them directly bound to the substrate, and part of them bound to other SiC grains. This interlayer is followed by an essentially different region of the coating as concerns the microstructure; this region consists of nanocrystalline diamond particles embedded in an amorphous carbon matrix. It is this heterogeneous microstructure to which we attribute (i) the good adhesion based upon the interface stabilizing SiC grains, and (ii) the high hardness and wear resistance based upon the diamond nanocrystals in the coating.