Water vapor adsorption kinetics on small and full scale zeolite coated adsorbers; A comparison
(2013)
A possibility to enhance both heat and mass transfer characteristics of an adsorber heat exchanger is to apply the adsorbent directly to its surface in form of a consolidated layer. As the majority of the available publications on the effect of both coating technology and adsorbent layer thickness on the adsorption kinetics deals with small scale adsorbent samples, the results obtained can only represent the best case design of an adsorber heat exchanger. This article presents, therefore, a comparison between the adsorption kinetics of water vapour on small as well as two different full scale coated adsorber heat exchanger types with AQSOA-Z02 layers of Mitsubishi Plastics Incorporation under quasi isobaric conditions of adsorption heat pumps. The small scale coated samples have a zeolite dry mass of 200 mg and layer thicknesses of 200, 300 and 500 μm while the full scale adsorbers have a coated zeolite mass between 1.5 and 2.5 kg and layer thicknesses of 150, 200, 300, 400 and 500 μm. In the investigated adsorption heat pump module, up to 52.7 and 57.3% of the equilibrium differential water loading measured with the small scale coated substrates have been obtained after an adsorption-evaporation times of 300 and 600 s, respectively.
This paper presents novel experimental methods for verification of both hydrothermal and mechanical stabilities of adsorbent coatings. Experiments have been carried out on zeolite-based coatings over aluminum substrates, prepared by a dip-coating technique developed at CNR-ITAE. Hydrothermal aging of several adsorbent coatings is ongoing. Adsorption and structural stability of some samples under test was successfully verified after 35000 aging cycles by isobars measurement and XRD analysis. Mechanical properties of coatings have been evaluated by applying different typologies of static and dynamic mechanical stresses. Results obtained have been compared with those achieved by subjecting adsorbent coatings prepared by Mitsubishi Plastic Incorporation (MPI) to the same characterization protocol. The comparison between the two types of coating returned that MPI coatings posses similar thermal stability and better mechanical strength than CNR-ITAE coatings.