Keywords
- Composite (1)
- Fiber-reinforced polymer (1)
- Filament winding (1)
- Split-disk (1)
- Tensile tests (1)
- Tubes (1)
Filament wound composite structures are widely used in the field of pressure vessels, tubes, pipelines or rocket cases. The mechanical behavior of these structures is typically different from those of flat laminated structures due to an alternating lay-up sequence, winding tension and manufacturing induced imperfections. However, design and analysis issues require the same engineering data as used for laminated structures in general. It has therefore become necessary to establish an accompanying quality assurance procedure following the production process to identify the material properties of the manufactured tubes especially for the single layer. Consequently, there are three different approaches of determining the elastic moduli and tensile strengths of a filament wound laminate. Either specimens are resected from a curved tube, from a tube with plane areas or standardized flat specimens are manufactured under deviating production conditions. All approaches entail disadvantages, whether in terms of manufacturing or testing parameters including geometry, lay-up sequence, porosity, fiber tension and load direction. This study presents the discrepancies in the determination of mechanical properties of a filament wound glass-fiber-reinforced polymer tube on curved or cylindrical specimens and flat specimens produced to meet the specifications of international standards. In order to obtain material properties not only in longitudinal but also in transverse direction of the tubes, the so-called split-disk tensile test modeled after ASTM Standard D 2290, is used with tube segments.The procedures of specimen production and preparation are described in detail. Material properties such as the fiber volume and void content of the composite specimens are conducted in order to consider quality and production differences. Finally tensile tests are performed and the results are compared and discussed.
High quality semi-finished products with reproducible properties of basaltic fibres are hardly available on the market. In order to examine the properties of basalt fibre reinforced plastics high quality specimens are necessary. The fibre volume content and the porosity of the produced specimen are used as the typical criteria to evaluate the achieved quality of the produced material. The effect of the geometrical properties of the different semi-finished products on the fibre volume contents is relatively small whereas the porosity content is considerably affected.