Refine
Year of publication
Document Type
- conference proceeding (article) (29)
- Article (16)
- Part of Periodical (6)
- conference talk (2)
- Part of a Book (1)
- conference proceeding (volume) (1)
Is part of the Bibliography
- no (55)
Keywords
- field emission (16)
- Current measurement (8)
- CATHODES (6)
- Iron (6)
- field emitter array (6)
- silicon (6)
- Etching (4)
- black silicon (4)
- Electron sources (3)
- FABRICATION (3)
Institute
Begutachtungsstatus
- peer-reviewed (40)
We report on gated p-type Si-tip array cathodes for implementation into field emission electron sources for sensor applications. Arrays of 16 and 100 tips with tip heights of 3 μm and tip radii below 30 nm with integrated gate electrodes concentrically positioned 2 μm below the tip apexes were fabricated using an improved process, which leads to an enhanced isolation layer quality with sufficient breakdown field strengths and low leakage currents. Integral measurements with a fixed grid potential of 400 V showed emission currents up to 35 μA for 100 tips at a cathode voltage of 150 V and an almost negligible parasitic gate current. The array with 16 p-type Si-tips showed a significant stabilization of the emission current in the range of 0.3 - 0.4 μA, for cathode voltages between 90 V and 150 V. The current fluctuation in this saturation regime was measured for 10 minutes and a value of less than ± 1% was observed. No degradation of the cathode was found after 6 hours of operation at a constant cathode voltage of 100 V and a constant grid voltage of 400 V.
Forschungsbericht 2016
(2016)
The authors report on the fabrication and characterization of p-type Si tip arrays with an integrated gate electrode for applications as field emission electron sources. After the reactive ion etching of the emitters, the combined thermal dry and wet oxidation was used for both the sharpening of the emitters and for the realization of an enhanced insulation layer. Au was evaporated in a self-aligned process as gate electrode. Arrays of 16 Si tips were fabricated with tip heights of about 3 μm and tip radii of about 20 nm with integrated gate electrode concentrically positioned ≈2 μm below the tip apex. Integral measurements with an additional anode showed improved field emission properties with a reproducible and stable emission behavior. A fast activation of the tips, low onset voltages of about 30 V, and moderate field emission currents up to 0.55 μA were noticed. The field emission parameters were calculated using the Fowler–Nordheim characteristics. A pronounced saturation regime was observed, and current fluctuations of less than ±1% were investigated for 30 min. Long-term measurements were carried out for a period of more than 8 h. In the first 6 h of operation, the authors observed a drift of the emission current from 0.35 to 0.55 μA caused by an increased emission surface.
Fabrication and simulation of silicon structures with high aspect ratio for field emission devices
(2014)
To obtain higher field enhancement factors of Si-tip structures, we present an improved fabrication process utilizing reactive-ion etching (RIE) with an inductively coupled plasma (ICP). In our design, a pillar under the tips is realized by a combination of RIE with ICP. With adjusted power settings (≈ 240 W) and step times (<; 5 s), vertical slopes with a low roughness of approximately 10 nm to 20 nm are possible. The remaining silicon is oxidized thermally to sharpen the emitters. A final tip radius of R <; 20 nm is obtained for the tips of the emitters. The pillar height HP can be mainly adjusted by the duration of the ICP-etching step. A total emitter height of H ≈ 6 μm with a pillar height of HP ≈ 5 μm is achieved. Simulations with COMSOL Multiphysics® are applied to calculate the field enhancement factor β. A two-dimensional model is used in rotational symmetry. In addition to the previous model, a pillar with a varying diameter ØP and height HP is added. A conventional emitter (H = 1 μm and R = 20 nm) placed on a pillar of the height HP ≈ 5 μm approximately results in a three times higher β-factor (β≈ 105). By decreasing the diameter ØP a slight increase of the β-factor is observed. However, the aspect ratio of the emitter mainly influences on the β-factor.
A compact vacuum-sealed field emission electron gun with an operation voltage below 5 kV is presented. With a 150 nm thick pyrolytic carbon membrane, a transmission of 40% at 5 kV is obtained. For more than 2500 h of continuous operation at an emission current of 100 nA, no significant increase (<50V ) and almost no degradation were found. From this measurement, a lifetime of more than 10 000 h at continuous operation with approximately a linear increase of the extraction voltage from about 545 V to about 730 V is predicted. This electron source enables application of field emitter arrays in poor vacuum or even ambient pressure.
ACKNOWLEDGMENT
This work was supported by the German Federal Ministry for Economic Affairs and Energy under Project No. ZF4081502GM8. C.P., R.L., M.H., and R.S. were supported by Grant No. ZF4562901GM8.
Influence of adsorbates on the performance of a field emitter array in a high voltage triode setup
(2017)
In the present work, black-silicon field emitter arrays (FEAs) are investigated regarding the influence of residual gas pressure on the characteristics and lifetime in the high voltage triode setup. Current-voltage-characteristics at different pressure levels are recorded and show a decreasing emission current with rising pressure. This decrease can be explained by an increase of the work function and charging of the emitter surface caused by adsorbates. The emission current can be restored to its initial value by heating of the FEA up to 110 °C during active emission. With this regeneration procedure, an extended lifetime from about 20 h to 440 h at a residual gas pressure of 10−5 mbar is achieved.
An electron source with an array of individually controllable single tips allows the observation of each emitter current simultaneously as well as the measurement of the integral current. Furthermore, the initial activation process of the individual tips and current distribution of the source can be examined. The Si cathode consists of an array of 2 x 2 conically shaped emitter structures on a borosilicate glass substrate. The emitters were fabricated by laser micromachining and wet etching. Integral field emission (FE) measurements were performed in a diode configuration in a vacuum chamber at pressures of about 10(-9) mbar with a self-aligned Si extraction grid, due to adjustment pins. The total emission current was regulated to a predefined value (4.0, 10, 20, 40, and 50 mu A) by an external regulating circuit and recorded individually during the measurement. The onset voltage for a current of 1 nA varied between 320 and 430 V. The voltage conversion factor is in the range of 7.6 x 10(4) cm(-1) to 1.3 x 10(5) cm(-1). Constant currentmeasurementsover a longer periodof time (1800 values with a sample rate of 0.5 Hz) were performed and show a total current fluctuation less than 0.6% due to the regulation circuit. Despite the stable total current in regulated operation, it was observed that the individual emitters fluctuate up to 75% for low (similar to 10(-8) A) and 5% for high (similar to 10(-5) A) currents.
The components for a silicon chip electron source were fabricated by laser micromachining using pulsed laser ablation and wet chemical cleaning and etching dips. The field emission electron source consists of a silicon field emission cathode with 4 × 4 conical shaped emitters with a height of 250 μm and a tip radius of about 50 nm, a 50 μm thick laser-structured mica spacer, and a silicon grid electrode with a grid periodicity of 200 μm and a bar width of 50 μm. These three components are combined to a single chip with the size of 14 × 10 mm2 and the thickness of 1 mm to form the electron source. Several of these devices were characterized in ultrahigh vacuum. Onset voltages of about 165 V and cathode currents of about 15 μA for voltages lower than 350 V were observed. Operating the electron source with an anode voltage of 500 V and an extraction grid voltage of 300 V yielded a cathode current of 4.5 μA ± 8.9%, an anode current of 4.0 μA ± 9.6%, and a corresponding grid transmittance of 89%. Regulating the anode current by the extraction grid voltage, an extremely stable anode current of 5.0 μA ± 0.017% was observed. A long-term measurement over 120 h was performed, and no significant degradation or failure was observed.
At the moment, only complicated techniques are known for the determination of array properties of field emitter arrays such as the number of active tips, the current distribution, or the individual tip radii. In this work, a method for extracting these parameters from integral measurement data is presented. A model describing the characteristics of a single emitter, including the saturation as a function of the applied voltage and the emitter radius, is developed. It is shown that experimental data of field emitter arrays can be represented as the sum of these functions and the characteristic parameters can be fitted to field emission data of an array. Using this method, the values of the radii as well as the parameters of distribution models can be determined directly. Analysis of experimental data from p-type Si emitter arrays shows that only 1–2% of the tips contribute significantly.
Extraction of the characteristics of current-limiting elements from field emission measurement data
(2017)
In this contribution, the authors will present an algorithm to extract the characteristics of nonideal field emission circuit elements from saturation-limited field emission measurement data. The method for calculating the voltage drop on current-limiting circuit elements is based on circuit theory as well as Newton's method. Since the only assumption the authors make on the current-limiting circuit is a connection in series, this method is applicable to most field emission data showing saturation. To be able to determine the significance of any parameter output, the uncertainties of data and extracted parameters as well as the parameter correlations are fully taken into account throughout the algorithm. N-type silicon samples with varying external serial resistors are analyzed. All results show a good agreement to the nominal resistor values. Additionally, several p-type samples are analyzed, showing a diodelike behavior. The extracted current-limiting characteristics of the p-type samples are in good agreement with a pn-junction model. The stability of the emission current of the p-type samples is measured by constant voltage measurements and compared to the extracted current-limiting characteristics. The application of the algorithm to measurement data shows that the given algorithm is a valuable tool to analyze field emission measurement data influenced by nonemissive processes.