The focus of this paper is the characterization of the influence of the temperature rates on the TMF lives. Therefore static and the dynamic calibrations of the temperature measurement devices were compared by a custom-built calibration specimen, which included five internal mantle thermocouples. Additionally the temperatures were measured on the specimens' surface. The experimental setups used were compared by executing TMF pre-test with the identical single-crystalline specimen. Subsequently TMF tests on coated single-crystalline Nickel-based superalloy PWA 1484 were carried out with temperature rates of 10K/s and 20 K/s. Finally the deviations of the determined TMF lives were evaluated.
The focus of this paper is the simulation of fatigue crack growth of the coated single crystalline nickel-based superalloy PWA 1484 under thermal mechanical loading. Thus, two physical models are superimposed in terms to firstly calculate the deformation behavior under instationary thermal and mechanical loading (TMF) and secondly to model crack propagation after initial brittle cracking of the coating layer on the basis of cyclic crack tip opening displacement (CTOD). All material parameters implemented in the models were evaluated from monotonic isothermal tensile and creep tests as well as from isothermal low cycle fatigue (LCF) experiments. The calculated fatigue crack growth was validated by in situ crack growth measurements using the beachmark technique. Hence, crack propagation initiated by the brittle coating system closely to the experimental results using rectangular flat specimen geometry instead of corner-crack (CC) specimens. The comparison of the simulated lifetimes to the experimental results provides remarkable accuracy of the physically-based lifetime model.
Repeated loadings may cause fatigue fractures in bony structures. Even if these failure types are known, data for trabecular bone exposed to cyclic loading are still insufficient as the majority of fatigue analyses on bone concentrate on cortical structures. Despite its highly anisotropic and inhomogeneous structure, trabecular bone is treated with continuum approaches in fatigue analyses. The underlying deformation and damage mechanism within trabecular specimens are not yet sufficiently investigated. In the present study different types of trabecular bone were loaded in monotonic and cyclic compression. In addition to the measurement of integral specimen deformations, optical deformation analysis was employed in order to obtain strain distributions at different scale levels, from the specimens' surface to the trabeculae level. These measurements allowed for the possibility of linking the macroscopic and microscopic mechanical behaviour of cancellous bone. Deformations were found to be highly inhomogeneous across the specimen. Furthermore strains were found to already localise at very low load levels and after few load cycles. Microcracks in individual trabeculae were induced in the very early stage of cyclic testing. The results provide evidence of the capability of the method to supply essential data on the failure behaviour of individual trabeculae in future studies.