Refine
Year of publication
Document Type
- conference proceeding (article) (41)
- Article (19)
- Part of Periodical (7)
- Part of a Book (1)
- conference talk (1)
Is part of the Bibliography
- no (69)
Keywords
- field emission (21)
- Current measurement (11)
- silicon (11)
- Iron (10)
- CATHODES (8)
- field emitter array (6)
- elemental semiconductors (5)
- Etching (4)
- FABRICATION (4)
- black silicon (4)
Institute
Begutachtungsstatus
- peer-reviewed (48)
Forschungsbericht 2013
(2014)
Forschungsbericht 2016
(2016)
Forschungsbericht 2017
(2017)
Forschungsbericht 2012
(2012)
Forschung 2019
(2019)
The authors report on the fabrication and characterization of p-type Si tip arrays with an integrated gate electrode for applications as field emission electron sources. After the reactive ion etching of the emitters, the combined thermal dry and wet oxidation was used for both the sharpening of the emitters and for the realization of an enhanced insulation layer. Au was evaporated in a self-aligned process as gate electrode. Arrays of 16 Si tips were fabricated with tip heights of about 3 μm and tip radii of about 20 nm with integrated gate electrode concentrically positioned ≈2 μm below the tip apex. Integral measurements with an additional anode showed improved field emission properties with a reproducible and stable emission behavior. A fast activation of the tips, low onset voltages of about 30 V, and moderate field emission currents up to 0.55 μA were noticed. The field emission parameters were calculated using the Fowler–Nordheim characteristics. A pronounced saturation regime was observed, and current fluctuations of less than ±1% were investigated for 30 min. Long-term measurements were carried out for a period of more than 8 h. In the first 6 h of operation, the authors observed a drift of the emission current from 0.35 to 0.55 μA caused by an increased emission surface.
Innovatives Verfahren zur Herstellung und Integration metallischer Nanokonen für die Feldemission
(2017)
In den letzten Jahren wurde am Institut für Elektromechanische Konstruktionen die Fabrikation und Integration von metallischen Nanodrähten und Nanokonen mittels Template-basierter Abscheidung erforscht. Diese Variante der in-situ Abscheidung von metallischen Nanostrukturen bietet eine Vielzahl von Anwendungsmöglichkeiten. Im Rahmen dieses Beitrags werden das Herstellungsverfahren zur Herstellung metallischer Nanokonen vorgestellt. Dies beinhaltet sowohl die Templatepräparation mittels asymmetrischen Ätzens als auch die anschließende Integration mittels galvanischer Abscheidung. Eine Anwendung der metallischen Nanokonen stellt die Verwendung als Feldemitter in der Vakuumelektronik dar. Es werden erste Messungen der Langzeitstabilität des Feldemissionsstromes der metallischen Konen präsentiert.
Fabrication and simulation of silicon structures with high aspect ratio for field emission devices
(2014)
To obtain higher field enhancement factors of Si-tip structures, we present an improved fabrication process utilizing reactive-ion etching (RIE) with an inductively coupled plasma (ICP). In our design, a pillar under the tips is realized by a combination of RIE with ICP. With adjusted power settings (≈ 240 W) and step times (<; 5 s), vertical slopes with a low roughness of approximately 10 nm to 20 nm are possible. The remaining silicon is oxidized thermally to sharpen the emitters. A final tip radius of R <; 20 nm is obtained for the tips of the emitters. The pillar height HP can be mainly adjusted by the duration of the ICP-etching step. A total emitter height of H ≈ 6 μm with a pillar height of HP ≈ 5 μm is achieved. Simulations with COMSOL Multiphysics® are applied to calculate the field enhancement factor β. A two-dimensional model is used in rotational symmetry. In addition to the previous model, a pillar with a varying diameter ØP and height HP is added. A conventional emitter (H = 1 μm and R = 20 nm) placed on a pillar of the height HP ≈ 5 μm approximately results in a three times higher β-factor (β≈ 105). By decreasing the diameter ØP a slight increase of the β-factor is observed. However, the aspect ratio of the emitter mainly influences on the β-factor.
A compact vacuum-sealed field emission electron gun with an operation voltage below 5 kV is presented. With a 150 nm thick pyrolytic carbon membrane, a transmission of 40% at 5 kV is obtained. For more than 2500 h of continuous operation at an emission current of 100 nA, no significant increase (<50V ) and almost no degradation were found. From this measurement, a lifetime of more than 10 000 h at continuous operation with approximately a linear increase of the extraction voltage from about 545 V to about 730 V is predicted. This electron source enables application of field emitter arrays in poor vacuum or even ambient pressure.