Refine
Year of publication
Document Type
- conference proceeding (article) (40)
- Article (17)
- Part of Periodical (4)
- Part of a Book (1)
- conference talk (1)
Is part of the Bibliography
- no (63)
Keywords
- field emission (20)
- silicon (11)
- Current measurement (10)
- Iron (9)
- CATHODES (7)
- field emitter array (7)
- elemental semiconductors (6)
- field emitter arrays (6)
- silicon tips (6)
- Etching (4)
Institute
Begutachtungsstatus
- peer-reviewed (46)
The homogeneity of emitters is very important for the performance of field emission (FE) devices. Reactive-ion etching (RIE) and oxidation have significant influences on the geometry of silicon tips. The RIE influences mainly the anisotropy of the emitters. Pressure has a strong impact on the anisotropic factor. Reducing the pressure results in a higher anisotropy, but the etch rate is also lower. A longer time of etching compensates this effect. Furthermore an improvement of homogeneity was observed. The impact of uprating is quite low for the anisotropic factor, but significant for the homogeneity. At low power the height and undercut of the emitters are more constant over the whole wafer. The oxidation itself is very homogeneous and has no observable effect on further variation of the homogeneity. This modified fabrication process allows solving the problem of inhomogeneity of previous field emission arrays.
The homogeneity of emitters is very important for the performance of field emission (FE) devices. Reactive-ion etching (RIE) and oxidation have significant influences on the geometry of silicon tips. The RIE influences mainly the anisotropy of the emitters. Pressure has a strong impact on the anisotropic factor. Reducing the pressure results in a higher anisotropy, but the etch rate is also lower. A longer time of etching compensates this effect. Furthermore an improvement of homogeneity was observed. The impact of uprating is quite low for the anisotropic factor, but significant for the homogeneity. At low power the height and undercut of the emitters are more constant over the whole wafer. The oxidation itself is very homogeneous and has no observable effect on further variation of the homogeneity. This modified fabrication process allows solving the problem of inhomogeneity of previous field emission arrays.
In this contribution we report on field emission (FE) cathodes based on thin-film LED-technology and surface texturing. The FE cathode can be used both as an n-GaN cathode with an electrical contact at the top side metallization as well as a pn-GaN diode contacting only the p-GaN layer at the bottom side of the structure. The local and integral FE properties of the textured surface of the LED structure were investigated. For n-GaN an integral emission current up to 1.0 μA at an electric field of 19 V/μm was achieved. The pn-GaN diode measurements showed an integral current saturation behavior with two orders of magnitude lower FE currents. Regulated voltage scans obtained by FE scanning microscopy revealed a well-distributed emission over the whole cathode area. Measurements under pulsed tunable laser illumination and moderate electric fields indicated charge carrier generation in the buried double-heterostructures at photon energies below 3.5 eV besides normal photoemission above 4.1 eV.
Microrods and microlines by three-dimensional epitaxially grown GaN for field emission cathodes
(2017)
The three-dimensional epitaxial technique allows the realization of gallium nitride lines in addition to the rods. To optimize the properties of GaN-based field emission cathodes further investigations and an improvement of the epitaxial process were performed. The microrods and microlines consist of a one-order higher n-doped gallium nitride in comparison to the gallium nitride layer on the sapphire substrate. The typical height of the microrods and -lines is about 5 μm. The field emission properties of these structures were investigated in diode configuration by integral field emission measurements at pressures below 10 -9 mbar. For the microrods (microlines) a voltage of 1100 V (2000 V) was measured for a field emission current of about 0.5 μA with an onset field of about 12 MV/m (24 MV/m). Furthermore, the field enhancement factors for microrods and -lines are in the range of 300 and 200, respectively.
A novel three-dimensional epitaxial technique allows on patterned substrates the realization of gallium nitride pillars, also known as nano- and microrods. The typical dimensions of the microrods are in the range of one micron for the radius of the hexagonal footprint and about 10 μm in height. The microrods consist of a semiconductor heterostructure with an n GaN core, a n-GaN shell, a p GaN shell and an intermediate quantum well layer. The field emission properties were investigated in diode configuration by integral field emission measurements in a vacuum chamber at pressures around 10 -9 mbar. The spacer was mica with a thickness of 50 μm. A metallized fine-meshed nitride grid (or a metallized Si-grid) was used as anode. A current of about 1 μA at a voltage of 1250 V (1750 V) was measured. An onset field of about 12.5 MV/m (20 MV/m) and field enhancement factors in the range of 200 to 500 (150 to 300) were found. The investigation with the fine-meshed grid showed an expected pronounced saturation region.
Spitzen- und Kantenemitter aus Silizium mit einem hohen Aspektverhältnis für Ionisationsgassensoren
(2014)
Durch die Optimierung von reaktivem Ionenätzen mit induktiv gekoppeltem Plasma ist die Herstellung von verschiedenen Siliziumkathoden mit hoher Anisotropie und hohem Aspektverhältnis für Feldemissionsanwendungen möglich. Simulationen mit COMSOL Multiphysics untermauern das Potential von solchen Spitzen- und Kantenfeldemittern. Die Ergebnisse der Simulation zeigen einen zwei- bis sechsfach höheren Feldüberhöhungsfaktor der tiefgeätzten Strukturen im Vergleich zu identischen Emittern ohne zusätzliche Tiefenätzung. Feldemissionsmessungen bestätigen die Simulationsergebnisse. Der modifizierte Herstellungsprozess der Feldemitter ermöglicht somit einen zuverlässigen Betrieb von Feldemissionselektronenquellen bei kleineren makroskopischen Feldstärken. Außerdem weisen die Messungen des Emissionsstroms im Sättigungsbereich eine weitgehende Unabhängigkeit vom elektrischen Feld auf. Lokale Feldemissionsmessungen ergeben dadurch eine deutliche Stromstabilisierung, welche über große Feldstärkenbereiche konstant bleibt. Die Nutzung der HAR-Emitter (high aspect ratio) ist damit eine gute Voraussetzung für einen zuverlässigen Betrieb der Emissionskathoden bei kleinen Feldstärken für die Anwendung in Ionisationsgassensoren.
Fabrication and simulation of silicon structures with high aspect ratio for field emission devices
(2014)
To obtain higher field enhancement factors of Si-tip structures, we present an improved fabrication process utilizing reactive-ion etching (RIE) with an inductively coupled plasma (ICP). In our design, a pillar under the tips is realized by a combination of RIE with ICP. With adjusted power settings (≈ 240 W) and step times (<; 5 s), vertical slopes with a low roughness of approximately 10 nm to 20 nm are possible. The remaining silicon is oxidized thermally to sharpen the emitters. A final tip radius of R <; 20 nm is obtained for the tips of the emitters. The pillar height HP can be mainly adjusted by the duration of the ICP-etching step. A total emitter height of H ≈ 6 μm with a pillar height of HP ≈ 5 μm is achieved. Simulations with COMSOL Multiphysics® are applied to calculate the field enhancement factor β. A two-dimensional model is used in rotational symmetry. In addition to the previous model, a pillar with a varying diameter ØP and height HP is added. A conventional emitter (H = 1 μm and R = 20 nm) placed on a pillar of the height HP ≈ 5 μm approximately results in a three times higher β-factor (β≈ 105). By decreasing the diameter ØP a slight increase of the β-factor is observed. However, the aspect ratio of the emitter mainly influences on the β-factor.