Refine
Year of publication
Document Type
- conference proceeding (article) (40)
- Article (17)
- Part of Periodical (4)
- Part of a Book (1)
- conference talk (1)
Is part of the Bibliography
- no (63)
Keywords
- field emission (20)
- silicon (11)
- Current measurement (10)
- Iron (9)
- CATHODES (7)
- field emitter array (7)
- elemental semiconductors (6)
- field emitter arrays (6)
- silicon tips (6)
- Etching (4)
Institute
Begutachtungsstatus
- peer-reviewed (46)
Forschungsbericht 2013
(2014)
Forschungsbericht 2016
(2016)
Forschungsbericht 2017
(2017)
The authors report on the fabrication and characterization of p-type Si tip arrays with an integrated gate electrode for applications as field emission electron sources. After the reactive ion etching of the emitters, the combined thermal dry and wet oxidation was used for both the sharpening of the emitters and for the realization of an enhanced insulation layer. Au was evaporated in a self-aligned process as gate electrode. Arrays of 16 Si tips were fabricated with tip heights of about 3 μm and tip radii of about 20 nm with integrated gate electrode concentrically positioned ≈2 μm below the tip apex. Integral measurements with an additional anode showed improved field emission properties with a reproducible and stable emission behavior. A fast activation of the tips, low onset voltages of about 30 V, and moderate field emission currents up to 0.55 μA were noticed. The field emission parameters were calculated using the Fowler–Nordheim characteristics. A pronounced saturation regime was observed, and current fluctuations of less than ±1% were investigated for 30 min. Long-term measurements were carried out for a period of more than 8 h. In the first 6 h of operation, the authors observed a drift of the emission current from 0.35 to 0.55 μA caused by an increased emission surface.
Fabrication and simulation of silicon structures with high aspect ratio for field emission devices
(2014)
To obtain higher field enhancement factors of Si-tip structures, we present an improved fabrication process utilizing reactive-ion etching (RIE) with an inductively coupled plasma (ICP). In our design, a pillar under the tips is realized by a combination of RIE with ICP. With adjusted power settings (≈ 240 W) and step times (<; 5 s), vertical slopes with a low roughness of approximately 10 nm to 20 nm are possible. The remaining silicon is oxidized thermally to sharpen the emitters. A final tip radius of R <; 20 nm is obtained for the tips of the emitters. The pillar height HP can be mainly adjusted by the duration of the ICP-etching step. A total emitter height of H ≈ 6 μm with a pillar height of HP ≈ 5 μm is achieved. Simulations with COMSOL Multiphysics® are applied to calculate the field enhancement factor β. A two-dimensional model is used in rotational symmetry. In addition to the previous model, a pillar with a varying diameter ØP and height HP is added. A conventional emitter (H = 1 μm and R = 20 nm) placed on a pillar of the height HP ≈ 5 μm approximately results in a three times higher β-factor (β≈ 105). By decreasing the diameter ØP a slight increase of the β-factor is observed. However, the aspect ratio of the emitter mainly influences on the β-factor.
A compact vacuum-sealed field emission electron gun with an operation voltage below 5 kV is presented. With a 150 nm thick pyrolytic carbon membrane, a transmission of 40% at 5 kV is obtained. For more than 2500 h of continuous operation at an emission current of 100 nA, no significant increase (<50V ) and almost no degradation were found. From this measurement, a lifetime of more than 10 000 h at continuous operation with approximately a linear increase of the extraction voltage from about 545 V to about 730 V is predicted. This electron source enables application of field emitter arrays in poor vacuum or even ambient pressure.
ACKNOWLEDGMENT
This work was supported by the German Federal Ministry for Economic Affairs and Energy under Project No. ZF4081502GM8. C.P., R.L., M.H., and R.S. were supported by Grant No. ZF4562901GM8.
Influence of adsorbates on the performance of a field emitter array in a high voltage triode setup
(2017)
In the present work, black-silicon field emitter arrays (FEAs) are investigated regarding the influence of residual gas pressure on the characteristics and lifetime in the high voltage triode setup. Current-voltage-characteristics at different pressure levels are recorded and show a decreasing emission current with rising pressure. This decrease can be explained by an increase of the work function and charging of the emitter surface caused by adsorbates. The emission current can be restored to its initial value by heating of the FEA up to 110 °C during active emission. With this regeneration procedure, an extended lifetime from about 20 h to 440 h at a residual gas pressure of 10−5 mbar is achieved.
The field electron emission characteristics of individual tips of a silicon field emitter array are analyzed. The array of conical‐shaped tips is fabricated on a p‐type silicon wafer by using reactive ion etching and sharpening oxidation. The tips are decorated with single tungsten nanoparticles at their apexes. Furthermore, the focused ion beam is also used to increase surface conductivity of some of the tips. Comparative measurements of field emission are performed by using the scanning anode probe field emission microscopy technique. All types of tips demonstrated emission activation consisting of a sudden current increase at a certain value of the applied voltage. Compared to the pristine tips, a noticeable reduction of the saturation effect in the current–voltage characteristics and a smaller light sensitivity for the decorated tips is found. For ion‐treated tips, saturation effects and light sensitivity are completely suppressed. Scanning electron microscopy observations reveal the formation of single nanoscale protrusions extending from the metal particles and from the apexes of bare ion‐treated tips after exposure under strong electric fields during the field emission measurements. The influence of protrusions growth on characteristics of silicon field emitter arrays is discussed.
The components for a silicon chip electron source were fabricated by laser micromachining using pulsed laser ablation and wet chemical cleaning and etching dips. The field emission electron source consists of a silicon field emission cathode with 4 × 4 conical shaped emitters with a height of 250 μm and a tip radius of about 50 nm, a 50 μm thick laser-structured mica spacer, and a silicon grid electrode with a grid periodicity of 200 μm and a bar width of 50 μm. These three components are combined to a single chip with the size of 14 × 10 mm2 and the thickness of 1 mm to form the electron source. Several of these devices were characterized in ultrahigh vacuum. Onset voltages of about 165 V and cathode currents of about 15 μA for voltages lower than 350 V were observed. Operating the electron source with an anode voltage of 500 V and an extraction grid voltage of 300 V yielded a cathode current of 4.5 μA ± 8.9%, an anode current of 4.0 μA ± 9.6%, and a corresponding grid transmittance of 89%. Regulating the anode current by the extraction grid voltage, an extremely stable anode current of 5.0 μA ± 0.017% was observed. A long-term measurement over 120 h was performed, and no significant degradation or failure was observed.
At the moment, only complicated techniques are known for the determination of array properties of field emitter arrays such as the number of active tips, the current distribution, or the individual tip radii. In this work, a method for extracting these parameters from integral measurement data is presented. A model describing the characteristics of a single emitter, including the saturation as a function of the applied voltage and the emitter radius, is developed. It is shown that experimental data of field emitter arrays can be represented as the sum of these functions and the characteristic parameters can be fitted to field emission data of an array. Using this method, the values of the radii as well as the parameters of distribution models can be determined directly. Analysis of experimental data from p-type Si emitter arrays shows that only 1–2% of the tips contribute significantly.