In this contribution we report on field emission (FE) cathodes based on thin-film LED-technology and surface texturing. The FE cathode can be used both as an n-GaN cathode with an electrical contact at the top side metallization as well as a pn-GaN diode contacting only the p-GaN layer at the bottom side of the structure. The local and integral FE properties of the textured surface of the LED structure were investigated. For n-GaN an integral emission current up to 1.0 μA at an electric field of 19 V/μm was achieved. The pn-GaN diode measurements showed an integral current saturation behavior with two orders of magnitude lower FE currents. Regulated voltage scans obtained by FE scanning microscopy revealed a well-distributed emission over the whole cathode area. Measurements under pulsed tunable laser illumination and moderate electric fields indicated charge carrier generation in the buried double-heterostructures at photon energies below 3.5 eV besides normal photoemission above 4.1 eV.
Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars.
We report on gated p-type Si-tip array cathodes for implementation into field emission electron sources for sensor applications. Arrays of 16 and 100 tips with tip heights of 3 μm and tip radii below 30 nm with integrated gate electrodes concentrically positioned 2 μm below the tip apexes were fabricated using an improved process, which leads to an enhanced isolation layer quality with sufficient breakdown field strengths and low leakage currents. Integral measurements with a fixed grid potential of 400 V showed emission currents up to 35 μA for 100 tips at a cathode voltage of 150 V and an almost negligible parasitic gate current. The array with 16 p-type Si-tips showed a significant stabilization of the emission current in the range of 0.3 - 0.4 μA, for cathode voltages between 90 V and 150 V. The current fluctuation in this saturation regime was measured for 10 minutes and a value of less than ± 1% was observed. No degradation of the cathode was found after 6 hours of operation at a constant cathode voltage of 100 V and a constant grid voltage of 400 V.