Refine
Year of publication
Document Type
- conference proceeding (article) (41)
- Article (19)
- Part of Periodical (7)
- Part of a Book (1)
- conference talk (1)
Is part of the Bibliography
- no (69)
Keywords
- field emission (21)
- Current measurement (11)
- silicon (11)
- Iron (10)
- CATHODES (8)
- field emitter array (6)
- elemental semiconductors (5)
- Etching (4)
- FABRICATION (4)
- black silicon (4)
Institute
Begutachtungsstatus
- peer-reviewed (48)
The finite element simulation program COMSOL Multiphysics® was used to simulate the emission efficiency of a silicon tip electron source in triode configuration for different geometries and electrode potentials. The simulation predicts a maximum emission efficiency of 84% for an optimized structure. In a second simulation a gate electrode was concentrically arranged above a single CNT column. Here, the efficiency was simulated as a function of gate hole geometry, electrode potentials and distances between the electrodes. The simulation shows that a conical shape of the gate hole results in an efficiency up to nearly 100%.
Silicon-based cathodes with precisely aligned field emitter arrays of sharp tips applicable for miniaturized electron sources were successfully fabricated and characterized. This was made possible by an improved fabrication process using wet thermal oxidation, wet etching, and reactive-ion etching steps with adjustable anisotropy. As substrate materials, both p-doped silicon and n-doped silicon were used. The cathode chips contain about 3 × 10 5 Si tips/cm 2 in a triangular array with tip heights of 2.5 μm, tip radii of less than 30 nm, and spacing of 20 μm. Well-aligned field emission (FE) and excellent homogeneity from all tips (i.e., 100% efficiency) and maximum stable currents of typically 0.1 μA (0.6 μA) for p (n)-type Si were reproducibly achieved. The current-voltage characteristics of the p-Si tips exhibit the expected saturation at around 10 nA with around ten times better current stability, whereas the n-Si tips show the usual Fowler-Nordheim behavior. Additional coating of the Si tips with 5-nm Cr and 10-nm Au layers resulted in improved stability and at least five times higher average FE current limits (about 3 μA) at about 30% higher operation voltage.
The electron current from field-emitting B-doped Si-tip arrays under illumination was studied. An improved cathode design with a patch of 271 tips yielded a reproducible cathode current between 0.2-2000 nA in the electric field range of 3.8-6.6 V/μm. The plateau in the Fowler-Nordheim plot shows the actual carrier depletion and leads to a very stable emission at ~1 μA with a current noise of less than 3.3 %. Color-filtered halogen lamp illumination was used to investigate the photo-sensitivity of the saturation current. The intensity-normalized current switching ratio increases nonlinearly with the photon energy. This hints either for secondary generation in the conduction band or deeper valence band excitation. The first is supported by a rough estimation of the quantum efficiency. Further experiments with a tunable laser and electron spectroscopy are planned.
In order to optimize our field-emitting silicon structures, the influence of geometric parameters like aspect ratio, aperture angle and curvature on the field enhancement factor was investigated by finite element simulations. A universal geometric model consisting of a rounded triangle and elliptic curvatures was taken for modeling a variety of different silicon tip as well as ridge structures. Whereas, a high dependency of the field enhancement on the aperture angle was found, the simulations show that the elliptic curvature affects the field enhancement only marginal.
In order to improve the uniformity and field emission stability of p-type silicon tip arrays for pulsed sensor applications, we have systematically studied the influence of the fabrication parameters on the tip shape and the specific operating conditions. Based on detailed design calculations of the field enhancement, we have fabricated a series of hexagonal arrays of B-doped Si-tips in a triangular arrangement, each containing a different number of tips (91, 575 and 1300) of 1 μm height, 20 nm apex radius, and 20 μm pitch. The field emission properties of both individual tips and complete arrays were investigated with by field emission scanning microscopy. The current plateaus of these tips typically occur at about 10 nA and 60 V/μm field level. In this carrier depletion range, single tips provide the highest current stability (<; 4%) and optical current switching ratios of ~2.5. Rather homogeneous emission of the tip arrays leads to an almost linear scaling of the saturation current (2 nA/tip) and to a much improved current stability (<; 1%) measured over 1 hour.
We have fabricated a test chip with various hexagonal arrays of B-doped Si tips (height ~ 3 μm, apex radius <; 30 nm, number 1-4447, resistivity 4 Ωcm, 100 orientation) in triangular arrangement (pitch 10 μm, density 1.16×10 6 cm -2 ) in order to systematically investigate the field emission current scaling with the number N of tips. Regulated voltage scans for 1 nA revealed rather efficient emission from nearly all tips of the arrays at an average field of 15 V/μm. The expected current plateau was always obtained at fields around 20 V/μm, but its width strongly increased with N. In this carrier depletion range, the single tip provided a much higher stability (<; 5%) of the current (2-3 nA) than at lower (>; 50 %) and higher currents (>; 30%). Integral current measurements of the hexagonal arrays resulted in a statistically improved current stability (<; 1%) but only a weak increase of the total current with N 0.28 yet. These results will be discussed with respect to the remaining inhomogeneity of the tips.
Forschungsbericht 2012
(2012)
Advanced Si-based semiconductor technology is most suitable to fabricate uniform nanostructures as integrated field emitter arrays for novel vacuum electronic devices. In order to improve the field emission homogeneity and stability of p-type silicon tip arrays for pulsed sensor applications, the authors have systematically studied the influence of the fabrication parameters on the tip shape and on the specific operating conditions. Based on detailed design calculations of the field enhancement, they have fabricated two series of hexagonal arrays of B-doped Si-tips in a triangular arrangement. The first (second) type contains three (four) patches with different number of tips (1, 91, 547 and 1, 19, 1027, 4447 for the first and second type, respectively) of about 1 (2.5) μm height, ∼20 (20) nm apex radius, and 20 (10) μm pitch. The field emission properties of both individual tips and complete arrays were investigated with a field emission scanning microscope at a pressure of 10−9 mbar. The current plateau of these tips typically occurs at about 10 (3) nA and around 65 (25) V/μm field level. In this carrier saturation range, single tips provide the highest current stability (<5%) and optical current switching ratio (∼2.5). Fairly homogeneous emission of the tip arrays leads to an undershooting of the expected linear scaling of the mean plateau current as well as to a much improved current stability (<1%).
The performance of free electron lasers depends on the brilliance of the electron source. Nowadays photo-cathodes (e.g. Cs2Te) are used despite of their high emittance. To develop robust and more brilliant cathodes we have built up an UHV system which enables systematic photoemission (PE) measurements with a tunable pulsed laser (hv) at high electric fields (E). First results on Au and Ag crystals revealed only low quantum efficiency (QE) due to fast electron relaxation. Hence, we have started QE(hv,E) investigations on n- and p-Si wafers. Resonant PE was observed above as well as below the work function O, which can be assigned to optical transitions in the electronic band structure or explained by thermally excited states at the bottom of the conduction band. As expected, only low QE values were achieved even for n-Si probably due to surface oxide. Moreover, a significant rise of the QE peaks above O were obtained for n-Si at E >8 MV/m but limited by the occurrence of parasitic field emission from dust particles.
We report on the field emission properties of GaN LED surfaces. The textured extraction facet acts both as light scattering layer in order to increase the light extraction efficiency of the LED as well as nanostructured cathode surface for the field emission (FE) of electrons. The LED emits blue light with a peak wavelength of around 450 nm. The FE properties were investigated by a scanning microscope. Integral measurements as well as regulated voltage scans for 1 nA FE current over an area of 400 * 400 µm2were used to investigate both overall and local FE properties. A high number of well-distributed emitters with an average field enhancement factor ß of 85 and stable integral emission currents up to 100 µA at an electric field of 80 V/µm (Øanode= 880 µm) were found. Photo-field-emission spectroscopy (PFES) using a tunable pulsed laser revealed an enhanced photo absorption of the InGaN/GaN quantum well structures near the emission wavelength of the LED (<3.5 eV), whereas at high photon energies (>4.1 eV) photoemission from the GaN surface was observed.