Precisely aligned arrays of sharp tip structures on top of elongated pillars were realized by using an improved fabrication process including an additional inductively-coupled-plasma reactive-ion etching step. Arrays of n-type and p-type silicon with 271 tips have been fabricated and investigated. Those structures have a total height of 5–6 µm and apex radii less than 20nm. Integral field emission measurements of the arrays yielded low onset-fields in the range of 8–12V=µm and field enhancement factors between 300 and 700. The I-E curves of n-type structures showed the usual Fowler-Nordheim behaviour, whereas p-type structures revealed a significant saturation region due to the limited number of electrons in the conduction band and a further carrier depletion effect caused by the pillar. The maximum integral current in the saturation region was 150 nA at fields above 30V=µm. An excellent stability of the emission current of less than ± 2% fluctuation was observed in the saturation region. For n-type Si a maximum integral current of 10 µA at 24V=µm and an average current stability with a fluctuation of ± 50% were measured.
Silicon tip arrays were fabricated by means of reactive ion etching followed by oxidation for final sharpening and molybdenum thin film coating. The field-emission (FE) properties of these Mo-coated p-Si tip arrays were systemically investigated by different measurement techniques. Integral measurements in diode configuration yielded a turn-on field (for 1 nA) of 22 V/μm and nearly stable FE currents up to 6.6 μA at 38 V/μm. The effective field enhancements factor extracted from the FN plots is about 180. Detailed investigations of these FE arrays were also performed by means of field emission scanning microscopy combined with electron microscopy. A rather limited efficiency of the tips (50% at 1500 V) and FE homogeneity (180 nA at 700 V) might be correlated with the varying morphology of the tips and the presence of oxides. Local I-V measurements of selected single tips revealed both activation and deactivation effects, which finally resulted in nearly reproducible I-V curves. Current stability measurements at a constant voltage showed rather large fluctuations (0.1-1 μA) of the FE current, which could be reduced up to 1.7% by using of a PID-regulated voltage source. SEM images showed unchanged tip shape after the current processing.
Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars.
An array of conical-shaped p-type silicon tips was fabricated by using reactive ion etching and sharpening oxidation. The apex of each tip was decorated by a tungsten hemispherical nanoparticle. Field emission properties of the tips were measured by a tungsten-needle anode positioned above the tip apex. Tips decorated with tungsten nanoparticles demonstrated a smaller saturation region in current-voltage characteristics compared to the pristine tips. An emission activation process, which consisted in sudden current increase at certain value of applied voltage, was observed for the decorated silicon tips. This behavior was explained by the formation of vertical protrusions extending from the metal particles revealed by scanning electron microscopy after field emission experiments.
Silicon-based cathodes with precisely aligned field emitter arrays of sharp tips applicable for miniaturized electron sources were successfully fabricated and characterized. This was made possible by an improved fabrication process using wet thermal oxidation, wet etching, and reactive-ion etching steps with adjustable anisotropy. As substrate materials, both p-doped silicon and n-doped silicon were used. The cathode chips contain about 3 × 10 5 Si tips/cm 2 in a triangular array with tip heights of 2.5 μm, tip radii of less than 30 nm, and spacing of 20 μm. Well-aligned field emission (FE) and excellent homogeneity from all tips (i.e., 100% efficiency) and maximum stable currents of typically 0.1 μA (0.6 μA) for p (n)-type Si were reproducibly achieved. The current-voltage characteristics of the p-Si tips exhibit the expected saturation at around 10 nA with around ten times better current stability, whereas the n-Si tips show the usual Fowler-Nordheim behavior. Additional coating of the Si tips with 5-nm Cr and 10-nm Au layers resulted in improved stability and at least five times higher average FE current limits (about 3 μA) at about 30% higher operation voltage.
The electron current from field-emitting B-doped Si-tip arrays under illumination was studied. An improved cathode design with a patch of 271 tips yielded a reproducible cathode current between 0.2-2000 nA in the electric field range of 3.8-6.6 V/μm. The plateau in the Fowler-Nordheim plot shows the actual carrier depletion and leads to a very stable emission at ~1 μA with a current noise of less than 3.3 %. Color-filtered halogen lamp illumination was used to investigate the photo-sensitivity of the saturation current. The intensity-normalized current switching ratio increases nonlinearly with the photon energy. This hints either for secondary generation in the conduction band or deeper valence band excitation. The first is supported by a rough estimation of the quantum efficiency. Further experiments with a tunable laser and electron spectroscopy are planned.
In order to optimize our field-emitting silicon structures, the influence of geometric parameters like aspect ratio, aperture angle and curvature on the field enhancement factor was investigated by finite element simulations. A universal geometric model consisting of a rounded triangle and elliptic curvatures was taken for modeling a variety of different silicon tip as well as ridge structures. Whereas, a high dependency of the field enhancement on the aperture angle was found, the simulations show that the elliptic curvature affects the field enhancement only marginal.
We have fabricated a test chip with various hexagonal arrays of B-doped Si tips (height ~ 3 μm, apex radius <; 30 nm, number 1-4447, resistivity 4 Ωcm, 100 orientation) in triangular arrangement (pitch 10 μm, density 1.16×10 6 cm -2 ) in order to systematically investigate the field emission current scaling with the number N of tips. Regulated voltage scans for 1 nA revealed rather efficient emission from nearly all tips of the arrays at an average field of 15 V/μm. The expected current plateau was always obtained at fields around 20 V/μm, but its width strongly increased with N. In this carrier depletion range, the single tip provided a much higher stability (<; 5%) of the current (2-3 nA) than at lower (>; 50 %) and higher currents (>; 30%). Integral current measurements of the hexagonal arrays resulted in a statistically improved current stability (<; 1%) but only a weak increase of the total current with N 0.28 yet. These results will be discussed with respect to the remaining inhomogeneity of the tips.
Semiconductor field emitters are suitable candidates for applications, which require a very stable field emission (FE) current and a high emission uniformity over the entire emission area. By using different materials and geometries, we are able to vary the FE characteristics within a wide range. Each specific application requires its own optimized design for the cathode as well as for the other parts of the FE electron source. To meet as many of these requirements as possible while using only a limited number of different prefabricated components, we established a modular system concept for our FE electron source. This allows the implementation of almost every cathode material. For first characterizations, we used gated p-type Si cathodes with 16 tips. We obtained stable FE currents of 0.4 μA for a grid-potential of 400 V and a gate potential of 100 V. Almost 100% of the electrons are emitted towards the grid-electrode. Parasitic leakage paths, as well as the electron emission towards the gate-electrode can be neglected. Approximately 10% of the electrons are transmitted through the grid and reach the external anode. This is in good agreement with the optical transmission through the grid-mesh.
Electron sources based on silicon field emitter arrays, produced in processes based on semiconductor technology, are good candidates for a miniaturized X-ray source. A key parameter for this application is the stability of the X-ray photon flux and, thus, the emission current. In the present work we have investigated the influence of the residual gas pressure and a resistor in series on the emission stability of a high aspect ratio n-type silicon emitter array with hybrid extraction electrode. An increase of current fluctuations was found for pressures above 10-6 mbar. High resistances in series to the emitter array alter the emission characteristics, but greatly suppress spikes in the emission current and improve its stability. This, however, strongly depends on the bias point. The field enhancement factor is not affected by the resistance. In a long term measurement the emission current was found to be constant after an initial phase of degradation.