Microrods and microlines by three-dimensional epitaxially grown GaN for field emission cathodes
(2017)
The three-dimensional epitaxial technique allows the realization of gallium nitride lines in addition to the rods. To optimize the properties of GaN-based field emission cathodes further investigations and an improvement of the epitaxial process were performed. The microrods and microlines consist of a one-order higher n-doped gallium nitride in comparison to the gallium nitride layer on the sapphire substrate. The typical height of the microrods and -lines is about 5 μm. The field emission properties of these structures were investigated in diode configuration by integral field emission measurements at pressures below 10 -9 mbar. For the microrods (microlines) a voltage of 1100 V (2000 V) was measured for a field emission current of about 0.5 μA with an onset field of about 12 MV/m (24 MV/m). Furthermore, the field enhancement factors for microrods and -lines are in the range of 300 and 200, respectively.
A novel three-dimensional epitaxial technique allows on patterned substrates the realization of gallium nitride pillars, also known as nano- and microrods. The typical dimensions of the microrods are in the range of one micron for the radius of the hexagonal footprint and about 10 μm in height. The microrods consist of a semiconductor heterostructure with an n GaN core, a n-GaN shell, a p GaN shell and an intermediate quantum well layer. The field emission properties were investigated in diode configuration by integral field emission measurements in a vacuum chamber at pressures around 10 -9 mbar. The spacer was mica with a thickness of 50 μm. A metallized fine-meshed nitride grid (or a metallized Si-grid) was used as anode. A current of about 1 μA at a voltage of 1250 V (1750 V) was measured. An onset field of about 12.5 MV/m (20 MV/m) and field enhancement factors in the range of 200 to 500 (150 to 300) were found. The investigation with the fine-meshed grid showed an expected pronounced saturation region.