The electron current from field-emitting B-doped Si-tip arrays under illumination was studied. An improved cathode design with a patch of 271 tips yielded a reproducible cathode current between 0.2-2000 nA in the electric field range of 3.8-6.6 V/μm. The plateau in the Fowler-Nordheim plot shows the actual carrier depletion and leads to a very stable emission at ~1 μA with a current noise of less than 3.3 %. Color-filtered halogen lamp illumination was used to investigate the photo-sensitivity of the saturation current. The intensity-normalized current switching ratio increases nonlinearly with the photon energy. This hints either for secondary generation in the conduction band or deeper valence band excitation. The first is supported by a rough estimation of the quantum efficiency. Further experiments with a tunable laser and electron spectroscopy are planned.
In order to optimize our field-emitting silicon structures, the influence of geometric parameters like aspect ratio, aperture angle and curvature on the field enhancement factor was investigated by finite element simulations. A universal geometric model consisting of a rounded triangle and elliptic curvatures was taken for modeling a variety of different silicon tip as well as ridge structures. Whereas, a high dependency of the field enhancement on the aperture angle was found, the simulations show that the elliptic curvature affects the field enhancement only marginal.
We have fabricated a test chip with various hexagonal arrays of B-doped Si tips (height ~ 3 μm, apex radius <; 30 nm, number 1-4447, resistivity 4 Ωcm, 100 orientation) in triangular arrangement (pitch 10 μm, density 1.16×10 6 cm -2 ) in order to systematically investigate the field emission current scaling with the number N of tips. Regulated voltage scans for 1 nA revealed rather efficient emission from nearly all tips of the arrays at an average field of 15 V/μm. The expected current plateau was always obtained at fields around 20 V/μm, but its width strongly increased with N. In this carrier depletion range, the single tip provided a much higher stability (<; 5%) of the current (2-3 nA) than at lower (>; 50 %) and higher currents (>; 30%). Integral current measurements of the hexagonal arrays resulted in a statistically improved current stability (<; 1%) but only a weak increase of the total current with N 0.28 yet. These results will be discussed with respect to the remaining inhomogeneity of the tips.