An array of conical-shaped p-type silicon tips was fabricated by using reactive ion etching and sharpening oxidation. The apex of each tip was decorated by a tungsten hemispherical nanoparticle. Field emission properties of the tips were measured by a tungsten-needle anode positioned above the tip apex. Tips decorated with tungsten nanoparticles demonstrated a smaller saturation region in current-voltage characteristics compared to the pristine tips. An emission activation process, which consisted in sudden current increase at certain value of applied voltage, was observed for the decorated silicon tips. This behavior was explained by the formation of vertical protrusions extending from the metal particles revealed by scanning electron microscopy after field emission experiments.
The electron current from field-emitting B-doped Si-tip arrays under illumination was studied. An improved cathode design with a patch of 271 tips yielded a reproducible cathode current between 0.2-2000 nA in the electric field range of 3.8-6.6 V/μm. The plateau in the Fowler-Nordheim plot shows the actual carrier depletion and leads to a very stable emission at ~1 μA with a current noise of less than 3.3 %. Color-filtered halogen lamp illumination was used to investigate the photo-sensitivity of the saturation current. The intensity-normalized current switching ratio increases nonlinearly with the photon energy. This hints either for secondary generation in the conduction band or deeper valence band excitation. The first is supported by a rough estimation of the quantum efficiency. Further experiments with a tunable laser and electron spectroscopy are planned.