The performance of free electron lasers depends on the brilliance of the electron source. Nowadays photo-cathodes (e.g. Cs2Te) are used despite of their high emittance. To develop robust and more brilliant cathodes we have built up an UHV system which enables systematic photoemission (PE) measurements with a tunable pulsed laser (hv) at high electric fields (E). First results on Au and Ag crystals revealed only low quantum efficiency (QE) due to fast electron relaxation. Hence, we have started QE(hv,E) investigations on n- and p-Si wafers. Resonant PE was observed above as well as below the work function O, which can be assigned to optical transitions in the electronic band structure or explained by thermally excited states at the bottom of the conduction band. As expected, only low QE values were achieved even for n-Si probably due to surface oxide. Moreover, a significant rise of the QE peaks above O were obtained for n-Si at E >8 MV/m but limited by the occurrence of parasitic field emission from dust particles.
Precisely aligned high-aspect-ratio (HAR) silicon tip arrays were fabricated using enhanced reactive ion etching with an inductively-coupled-plasma followed by a sharpening oxidation. A gold thin film was then sputtered only on the tips of the HAR structures. Field-emission (FE) properties from Au-coated HAR p-Si tip array cathodes have been systematically investigated by means of field emission scanning microscopy (FESM). A rather high efficiency of the HAR Si structures (71% at 550 V), but limited homogeneous FE with currents of 1-600 nA might be correlated with the varying geometry of the tips and the presence of oxides. I-V measurements of single Au-coated HAR emitters revealed activation effects and the saturation current region at 3 nA. An increase of the saturation current by 4 orders of magnitude was observed during 20 hours of conditioning at constant voltage, which finally resulted in nearly reproducible FN curves with a ß-factor of 473. An excellent stability of the emission current of less than 1 % was obtained during the additional long-time conditioning at constant voltage. Optical switching under halogen lamp illumination resulted in at least 2 times higher saturation currents and showed a linear dependence of the FE current on the light color temperature.
We have investigated the properties of single n- and p-type black silicon (b-Si) pillars with a height of 20 μ m under strong electric field and halogen lamp or laser illumination. For both type of b-Si pillar structures, I-V measurements revealed strong activation effects, which consisted in sudden current increases during the first up/down voltage sweeps. The maximum reproducible emission current from a single n-type b-Si pillar structure was about 15 μ A. A pronounced saturation region at 240 nA was observed for a single p-type b-Si pillar. The current fluctuation over time showed a standard deviation of 28% and 2.5% for n- and p-type single b-Si pillar structures, respectively. Optical switching under halogen lamp illumination resulted in at least 3 times higher saturation currents and showed a linear dependence of the FE current on the laser power.
An array of conical-shaped p-type silicon tips was fabricated by using reactive ion etching and sharpening oxidation. The apex of each tip was decorated by a tungsten hemispherical nanoparticle. Field emission properties of the tips were measured by a tungsten-needle anode positioned above the tip apex. Tips decorated with tungsten nanoparticles demonstrated a smaller saturation region in current-voltage characteristics compared to the pristine tips. An emission activation process, which consisted in sudden current increase at certain value of applied voltage, was observed for the decorated silicon tips. This behavior was explained by the formation of vertical protrusions extending from the metal particles revealed by scanning electron microscopy after field emission experiments.
We have carried out systematic investigations of p-type black Si field emitter arrays under laser illumination. As expected the current-voltage characteristic revealed a strong saturation providing a high photosensitivity, which had a maximum on-off ratio of 43 at a maximum current of 13 μA. The saturation current was stable in the dark as well as under illumination with fluctuations <;0.7%. Results from time-resolved measurements of the photo-sensitivity showed a rather fast response but a long decay time. Electron spectra in the dark and under laser illumination revealed the origin of the emission.
The electron current from field-emitting B-doped Si-tip arrays under illumination was studied. An improved cathode design with a patch of 271 tips yielded a reproducible cathode current between 0.2-2000 nA in the electric field range of 3.8-6.6 V/μm. The plateau in the Fowler-Nordheim plot shows the actual carrier depletion and leads to a very stable emission at ~1 μA with a current noise of less than 3.3 %. Color-filtered halogen lamp illumination was used to investigate the photo-sensitivity of the saturation current. The intensity-normalized current switching ratio increases nonlinearly with the photon energy. This hints either for secondary generation in the conduction band or deeper valence band excitation. The first is supported by a rough estimation of the quantum efficiency. Further experiments with a tunable laser and electron spectroscopy are planned.
Photosensitivity of single lightly p-doped, highly p-doped, with an integrated p/n junction and intrinsic high-aspect-ratio (HAR) silicon tips was investigated in an ultra-high vacuum environment. The current-voltage characteristics (I-V) of the lightly doped p-type HAR tips showed a characteristic current saturation at around 10-12 nA, whereas the HAR Si tips with p/n junction showed similar saturation phenomena, however, at much smaller current values starting at ~20-30 pA. Optical switching under a halogen lamp illumination resulted in at least 2-4 times higher saturation currents and showed a linear dependence between the illumination power and the FE current, for both types of structures. In case of the highly p-doped HAR tips optical current switching effects, i. e. current saturation, were observed at rather low current levels 1-2 pA. Intrinsic HAR Si-tips showed relative unstable field emission behavior without a clear evidence of the photosensitivity.