Refine
Document Type
- conference proceeding (article) (9)
- Article (5)
- Part of Periodical (1)
Is part of the Bibliography
- no (15)
Keywords
- field emission (6)
- Iron (5)
- silicon (5)
- CATHODES (4)
- Current measurement (4)
- photoemission (3)
- Etching (2)
- FABRICATION (2)
- GEOMETRY (2)
- Vacuum technology (2)
Institute
Begutachtungsstatus
- peer-reviewed (12)
Advanced Si-based semiconductor technology is most suitable to fabricate uniform nanostructures as integrated field emitter arrays for novel vacuum electronic devices. In order to improve the field emission homogeneity and stability of p-type silicon tip arrays for pulsed sensor applications, the authors have systematically studied the influence of the fabrication parameters on the tip shape and on the specific operating conditions. Based on detailed design calculations of the field enhancement, they have fabricated two series of hexagonal arrays of B-doped Si-tips in a triangular arrangement. The first (second) type contains three (four) patches with different number of tips (1, 91, 547 and 1, 19, 1027, 4447 for the first and second type, respectively) of about 1 (2.5) μm height, ∼20 (20) nm apex radius, and 20 (10) μm pitch. The field emission properties of both individual tips and complete arrays were investigated with a field emission scanning microscope at a pressure of 10−9 mbar. The current plateau of these tips typically occurs at about 10 (3) nA and around 65 (25) V/μm field level. In this carrier saturation range, single tips provide the highest current stability (<5%) and optical current switching ratio (∼2.5). Fairly homogeneous emission of the tip arrays leads to an undershooting of the expected linear scaling of the mean plateau current as well as to a much improved current stability (<1%).
Spitzen- und Kantenemitter aus Silizium mit einem hohen Aspektverhältnis für Ionisationsgassensoren
(2014)
Durch die Optimierung von reaktivem Ionenätzen mit induktiv gekoppeltem Plasma ist die Herstellung von verschiedenen Siliziumkathoden mit hoher Anisotropie und hohem Aspektverhältnis für Feldemissionsanwendungen möglich. Simulationen mit COMSOL Multiphysics untermauern das Potential von solchen Spitzen- und Kantenfeldemittern. Die Ergebnisse der Simulation zeigen einen zwei- bis sechsfach höheren Feldüberhöhungsfaktor der tiefgeätzten Strukturen im Vergleich zu identischen Emittern ohne zusätzliche Tiefenätzung. Feldemissionsmessungen bestätigen die Simulationsergebnisse. Der modifizierte Herstellungsprozess der Feldemitter ermöglicht somit einen zuverlässigen Betrieb von Feldemissionselektronenquellen bei kleineren makroskopischen Feldstärken. Außerdem weisen die Messungen des Emissionsstroms im Sättigungsbereich eine weitgehende Unabhängigkeit vom elektrischen Feld auf. Lokale Feldemissionsmessungen ergeben dadurch eine deutliche Stromstabilisierung, welche über große Feldstärkenbereiche konstant bleibt. Die Nutzung der HAR-Emitter (high aspect ratio) ist damit eine gute Voraussetzung für einen zuverlässigen Betrieb der Emissionskathoden bei kleinen Feldstärken für die Anwendung in Ionisationsgassensoren.
Semiconductor field emitters are suitable candidates for applications, which require a very stable field emission (FE) current and a high emission uniformity over the entire emission area. By using different materials and geometries, we are able to vary the FE characteristics within a wide range. Each specific application requires its own optimized design for the cathode as well as for the other parts of the FE electron source. To meet as many of these requirements as possible while using only a limited number of different prefabricated components, we established a modular system concept for our FE electron source. This allows the implementation of almost every cathode material. For first characterizations, we used gated p-type Si cathodes with 16 tips. We obtained stable FE currents of 0.4 μA for a grid-potential of 400 V and a gate potential of 100 V. Almost 100% of the electrons are emitted towards the grid-electrode. Parasitic leakage paths, as well as the electron emission towards the gate-electrode can be neglected. Approximately 10% of the electrons are transmitted through the grid and reach the external anode. This is in good agreement with the optical transmission through the grid-mesh.
We have investigated the properties of black Si field emitter arrays under strong electric fields and laser illumination. A low onset field of 1.8 MV/m for an emission current of 1 nA was obtained. A pronounced saturation region of the dark and photo-enhanced current was observed, which provided a short-term stability of 0.1% at 0.4 μA and 0.7% at 1.0 μA, respectively. As maximum value for the photosensitivity, an on-off current switching ratio of 43 reaching about 13 μA was achieved at a laser power of 15 mW. Electron spectra in the dark and under laser illumination are presented, showing a current and light-sensitive voltage drop across the emitters as well as hints for hot electron emission.
We have carried out systematic investigations of p-type black Si field emitter arrays under laser illumination. As expected the current-voltage characteristic revealed a strong saturation providing a high photosensitivity, which had a maximum on-off ratio of 43 at a maximum current of 13 μA. The saturation current was stable in the dark as well as under illumination with fluctuations <;0.7%. Results from time-resolved measurements of the photo-sensitivity showed a rather fast response but a long decay time. Electron spectra in the dark and under laser illumination revealed the origin of the emission.
Silicon-based cathodes with precisely aligned field emitter arrays of sharp tips applicable for miniaturized electron sources were successfully fabricated and characterized. This was made possible by an improved fabrication process using wet thermal oxidation, wet etching, and reactive-ion etching steps with adjustable anisotropy. As substrate materials, both p-doped silicon and n-doped silicon were used. The cathode chips contain about 3 × 10 5 Si tips/cm 2 in a triangular array with tip heights of 2.5 μm, tip radii of less than 30 nm, and spacing of 20 μm. Well-aligned field emission (FE) and excellent homogeneity from all tips (i.e., 100% efficiency) and maximum stable currents of typically 0.1 μA (0.6 μA) for p (n)-type Si were reproducibly achieved. The current-voltage characteristics of the p-Si tips exhibit the expected saturation at around 10 nA with around ten times better current stability, whereas the n-Si tips show the usual Fowler-Nordheim behavior. Additional coating of the Si tips with 5-nm Cr and 10-nm Au layers resulted in improved stability and at least five times higher average FE current limits (about 3 μA) at about 30% higher operation voltage.
Precisely aligned arrays of sharp tip structures on top of elongated pillars were realized by using an improved fabrication process including an additional inductively-coupled-plasma reactive-ion etching step. Arrays of n-type and p-type silicon with 271 tips have been fabricated and investigated. Those structures have a total height of 5–6 µm and apex radii less than 20nm. Integral field emission measurements of the arrays yielded low onset-fields in the range of 8–12V=µm and field enhancement factors between 300 and 700. The I-E curves of n-type structures showed the usual Fowler-Nordheim behaviour, whereas p-type structures revealed a significant saturation region due to the limited number of electrons in the conduction band and a further carrier depletion effect caused by the pillar. The maximum integral current in the saturation region was 150 nA at fields above 30V=µm. An excellent stability of the emission current of less than ± 2% fluctuation was observed in the saturation region. For n-type Si a maximum integral current of 10 µA at 24V=µm and an average current stability with a fluctuation of ± 50% were measured.
Forschungsbericht 2012
(2012)
Arrays of black silicon field emission pillar structures were fabricated on p-type silicon substrates. Two types of samples with the same number of pillars (arrays of 10 × 10) but different pillar heights (8 and 20 μm) were prepared as well as a black silicon reference sample without pillars. The field emission properties of these cathodes were investigated both by means of integral current-voltage measurements and by field emission scanning microscopy. Samples with a pillar height of 20 μm revealed onset fields as low as 6.4 V/μm, field enhancement factors up to 800, and emission currents up to 8 μA at an applied field of 20 V/μm. Due to the p-type material, a saturation of the emission current for fields above 11 V/μm was observed. This saturation leads to a stable operation with a current fluctuation of less than ±8%. It was found that samples with a pillar height of 20 μm showed improved emission characteristics compared to samples with a pillar height of 8 μm or without pillars. The voltage maps revealed an increased emission homogeneity after a “burn-in” sequence of the sample. The current map showed that a few of the pillars dominate the emission. Integral current stability measurements were performed under different vacuum pressures, in order to investigate altered emission behavior and a potential degradation of the emitters. At pressures above 10−6 mbar, the sample starts to degrade irreversibly. Nevertheless, even after a harsh treatment over 30 min at 5 × 10−5 mbar and at an applied field of 23 V/μm, the cathode was still operating, and did not fail during further operation over 20 h at 5 × 10−8 mbar and at an applied field of 28 V/μm.
In this contribution we report on field emission (FE) cathodes based on thin-film LED-technology and surface texturing. The FE cathode can be used both as an n-GaN cathode with an electrical contact at the top side metallization as well as a pn-GaN diode contacting only the p-GaN layer at the bottom side of the structure. The local and integral FE properties of the textured surface of the LED structure were investigated. For n-GaN an integral emission current up to 1.0 μA at an electric field of 19 V/μm was achieved. The pn-GaN diode measurements showed an integral current saturation behavior with two orders of magnitude lower FE currents. Regulated voltage scans obtained by FE scanning microscopy revealed a well-distributed emission over the whole cathode area. Measurements under pulsed tunable laser illumination and moderate electric fields indicated charge carrier generation in the buried double-heterostructures at photon energies below 3.5 eV besides normal photoemission above 4.1 eV.
We have investigated the properties of single n- and p-type black silicon (b-Si) pillars with a height of 20 μ m under strong electric field and halogen lamp or laser illumination. For both type of b-Si pillar structures, I-V measurements revealed strong activation effects, which consisted in sudden current increases during the first up/down voltage sweeps. The maximum reproducible emission current from a single n-type b-Si pillar structure was about 15 μ A. A pronounced saturation region at 240 nA was observed for a single p-type b-Si pillar. The current fluctuation over time showed a standard deviation of 28% and 2.5% for n- and p-type single b-Si pillar structures, respectively. Optical switching under halogen lamp illumination resulted in at least 3 times higher saturation currents and showed a linear dependence of the FE current on the laser power.
Precisely aligned high-aspect-ratio (HAR) silicon tip arrays were fabricated using enhanced reactive ion etching with an inductively-coupled-plasma followed by a sharpening oxidation. A gold thin film was then sputtered only on the tips of the HAR structures. Field-emission (FE) properties from Au-coated HAR p-Si tip array cathodes have been systematically investigated by means of field emission scanning microscopy (FESM). A rather high efficiency of the HAR Si structures (71% at 550 V), but limited homogeneous FE with currents of 1-600 nA might be correlated with the varying geometry of the tips and the presence of oxides. I-V measurements of single Au-coated HAR emitters revealed activation effects and the saturation current region at 3 nA. An increase of the saturation current by 4 orders of magnitude was observed during 20 hours of conditioning at constant voltage, which finally resulted in nearly reproducible FN curves with a ß-factor of 473. An excellent stability of the emission current of less than 1 % was obtained during the additional long-time conditioning at constant voltage. Optical switching under halogen lamp illumination resulted in at least 2 times higher saturation currents and showed a linear dependence of the FE current on the light color temperature.
Extraction of the characteristics of current-limiting elements from field emission measurement data
(2017)
In this contribution, the authors will present an algorithm to extract the characteristics of nonideal field emission circuit elements from saturation-limited field emission measurement data. The method for calculating the voltage drop on current-limiting circuit elements is based on circuit theory as well as Newton's method. Since the only assumption the authors make on the current-limiting circuit is a connection in series, this method is applicable to most field emission data showing saturation. To be able to determine the significance of any parameter output, the uncertainties of data and extracted parameters as well as the parameter correlations are fully taken into account throughout the algorithm. N-type silicon samples with varying external serial resistors are analyzed. All results show a good agreement to the nominal resistor values. Additionally, several p-type samples are analyzed, showing a diodelike behavior. The extracted current-limiting characteristics of the p-type samples are in good agreement with a pn-junction model. The stability of the emission current of the p-type samples is measured by constant voltage measurements and compared to the extracted current-limiting characteristics. The application of the algorithm to measurement data shows that the given algorithm is a valuable tool to analyze field emission measurement data influenced by nonemissive processes.
Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars.
Silicon tip arrays were fabricated by means of reactive ion etching followed by oxidation for final sharpening and molybdenum thin film coating. The field-emission (FE) properties of these Mo-coated p-Si tip arrays were systemically investigated by different measurement techniques. Integral measurements in diode configuration yielded a turn-on field (for 1 nA) of 22 V/μm and nearly stable FE currents up to 6.6 μA at 38 V/μm. The effective field enhancements factor extracted from the FN plots is about 180. Detailed investigations of these FE arrays were also performed by means of field emission scanning microscopy combined with electron microscopy. A rather limited efficiency of the tips (50% at 1500 V) and FE homogeneity (180 nA at 700 V) might be correlated with the varying morphology of the tips and the presence of oxides. Local I-V measurements of selected single tips revealed both activation and deactivation effects, which finally resulted in nearly reproducible I-V curves. Current stability measurements at a constant voltage showed rather large fluctuations (0.1-1 μA) of the FE current, which could be reduced up to 1.7% by using of a PID-regulated voltage source. SEM images showed unchanged tip shape after the current processing.