A compact vacuum-sealed field emission electron gun with an operation voltage below 5 kV is presented. With a 150 nm thick pyrolytic carbon membrane, a transmission of 40% at 5 kV is obtained. For more than 2500 h of continuous operation at an emission current of 100 nA, no significant increase (<50V ) and almost no degradation were found. From this measurement, a lifetime of more than 10 000 h at continuous operation with approximately a linear increase of the extraction voltage from about 545 V to about 730 V is predicted. This electron source enables application of field emitter arrays in poor vacuum or even ambient pressure.
ACKNOWLEDGMENT
This work was supported by the German Federal Ministry for Economic Affairs and Energy under Project No. ZF4081502GM8. C.P., R.L., M.H., and R.S. were supported by Grant No. ZF4562901GM8.
The components for a silicon chip electron source were fabricated by laser micromachining using pulsed laser ablation and wet chemical cleaning and etching dips. The field emission electron source consists of a silicon field emission cathode with 4 × 4 conical shaped emitters with a height of 250 μm and a tip radius of about 50 nm, a 50 μm thick laser-structured mica spacer, and a silicon grid electrode with a grid periodicity of 200 μm and a bar width of 50 μm. These three components are combined to a single chip with the size of 14 × 10 mm2 and the thickness of 1 mm to form the electron source. Several of these devices were characterized in ultrahigh vacuum. Onset voltages of about 165 V and cathode currents of about 15 μA for voltages lower than 350 V were observed. Operating the electron source with an anode voltage of 500 V and an extraction grid voltage of 300 V yielded a cathode current of 4.5 μA ± 8.9%, an anode current of 4.0 μA ± 9.6%, and a corresponding grid transmittance of 89%. Regulating the anode current by the extraction grid voltage, an extremely stable anode current of 5.0 μA ± 0.017% was observed. A long-term measurement over 120 h was performed, and no significant degradation or failure was observed.