Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars.
Electron sources based on silicon field emitter arrays, produced in processes based on semiconductor technology, are good candidates for a miniaturized X-ray source. A key parameter for this application is the stability of the X-ray photon flux and, thus, the emission current. In the present work we have investigated the influence of the residual gas pressure and a resistor in series on the emission stability of a high aspect ratio n-type silicon emitter array with hybrid extraction electrode. An increase of current fluctuations was found for pressures above 10-6 mbar. High resistances in series to the emitter array alter the emission characteristics, but greatly suppress spikes in the emission current and improve its stability. This, however, strongly depends on the bias point. The field enhancement factor is not affected by the resistance. In a long term measurement the emission current was found to be constant after an initial phase of degradation.