- Single-crystal Pd nanowires with typically 100 nm diameters and lengths from several micrometers to tens of micrometers were grown on Al 2 O 3 substrates in a furnace with Ar atmosphere. Integral field emission measurements of such samples after Pd coating (~10 nm) were performed in a diode configuration with a 50 μm mica spacer in a vacuum chamber at pressures of about 10 -9 mbar. The IVSingle-crystal Pd nanowires with typically 100 nm diameters and lengths from several micrometers to tens of micrometers were grown on Al 2 O 3 substrates in a furnace with Ar atmosphere. Integral field emission measurements of such samples after Pd coating (~10 nm) were performed in a diode configuration with a 50 μm mica spacer in a vacuum chamber at pressures of about 10 -9 mbar. The IV measurement of the sample shows an integral emission current up to 2 μA at a voltage of 500 V (10 MV/m) and an onset voltage for a current of 1 nA of about 275 V. The corresponding Fowler-Nordheim plot show a linear behavior, like expected for a metal needle.…