TY - CHAP A1 - Maiwald, Frederik A1 - Tröger, Johannes A1 - Hierl, Stefan T1 - Automated weld seam evaluation and 2D simulation parameter calibration for absorber-free laser transmission welding T2 - Lasers in Manufacturing Conference (LIM 2023), 26. Juni bis 29. Juni 2023, München N2 - Absorber-free laser transmission welding enables clean and precise joining of plastics without additives or adhesives. It is therefore well suited to produce optical and medical devices, which place high demands on cleanliness and accuracy. However, the weld usually has an undesirably large vertical expansion, causing bulges and distortion. To improve this, the intensity distribution of the laser beam as well as the processing strategy must be adapted. Due to the complexity, this is aided by process simulation. However, simulation parameter calibration and verification are usually done considering the seam width and height, which is of limited significance. To overcome this, we propose a new method for image processing of microtome sections, determining the spatially resolved geometry of the weld. Thus, the deviation between experiment and simulation can be calculated pixel by pixel. This spatially resolved value is predestined for the calibration of the simulation parameters: For a parameter field with 18 different settings, the total deviation between experiment and simulation is less than 11 % after calibration. KW - plastics welding KW - image processing KW - simulation KW - optimization Y1 - 2023 UR - https://www.wlt.de/sites/default/files/2023-09/Contribution_122.pdf PB - Wissenschaftliche Gesellschaft Lasertechnik und Photonik e.V. (WLT) ER - TY - GEN A1 - Grad, Marius A1 - Hahn, Konstantin A1 - Noster, Ulf A1 - Spieß, Lothar T1 - Increasing the lifetime of titanium implants through a diffusion-controlled surface treatment T2 - Thüringer Werkstofftag 2023, 14. März 2023, ILmenau Y1 - 2023 U6 - https://doi.org/10.13140/RG.2.2.35933.59360 ER - TY - CHAP A1 - Meisner, Dennis A1 - Forstner, Lukas A1 - Kaftiranis, Nikitas A1 - Hierl, Stefan T1 - Investigation of process improvements through laser preheating in extrusion-based additive manufacturing process T2 - Lasers in Manufacturing Conference (LIM 2023), 26. Juni bis 29. Juni 2023, München N2 - Fused layer modeling (FLM) is widely used and is gaining more acceptance in the industry mainly due to its material variety and low costs. However, the usage is limited by a process-related anisotropy of the produced parts. The strength and ductility of the printed parts are significantly lower in the build-up direction than perpendicular to it. This is caused by insufficient interlayer bonding resulting from a reduced surface temperature in the process zone. To overcome this problem, a diode laser is integrated into the conventional FLM process to increase the surface temperature between the already printed surface and the newly applied substrate directly at the deposition zone. The investigations carried out show a significant improvement in the mesostructure, as well as a clear reduction in the anisotropy of the printed test specimens. KW - fused layer modeling KW - laser preheating KW - anisotropy KW - interlayer bonding KW - mesostructure Y1 - 2023 UR - https://www.wlt.de/sites/default/files/2023-09/Contribution_140.pdf PB - Wissenschaftliche Gesellschaft Lasertechnik und Photonik e.V. (WLT) ER - TY - JOUR A1 - Reindl, Thomas A1 - Meisner, Dennis A1 - Hierl, Stefan T1 - Benchmarking of plastic-based Additive Manufacturing Processes JF - RTejournal - Forum für Rapid Technologie N2 - Additive Manufacturing (AM) is a future-oriented manufacturing technology that is experiencing an enormous boom in the times of Industry 4.0. As a result, various AM technologies and printer models from different manufacturers are entering the market over a short time span. With the advancing establishment of this manufacturing technology for series applications, the expectations and requirements of the fabricated components are also increasing. However, a major challenge is the application-specific selection of the most suitable AM process due to a lack of comparable data. Furthermore, there needs to be more know-how regarding the geometrical and mechanical characteristics of AM parts. This paper addresses this problem by comparing the three most common plasticbased AM processes in the areas of surface quality, dimensional accuracy, and mechanical properties. Roughness measurements, evaluation of a benchmark artifact, tensile tests, and load increase tests are carried out. Based on the results, the individual possibilities and limitations of the compared AM processes can be detected. KW - Additive Manufacturing KW - benchmark artifact KW - dimensional accuracy KW - Fused Layer Modeling KW - mechanical properties KW - Multi Jet Fusion KW - process benchmark KW - Selective Laser Sintering KW - surface quality Y1 - 2023 U6 - https://doi.org/https://doi.org/10.58134/fh-aachen-rte_2023_002 PB - Fachhochschule Aachen ER - TY - JOUR A1 - Kuettner, Andreas A1 - Raths, Max A1 - Fischer, Samuel A1 - Laumer, Tobias T1 - Heat staking of polymer parts generated by fused layer modeling JF - The International Journal of Advanced Manufacturing Technology N2 - Heat staking is a joining technology by which thermoplastic pins are formed by force and temperature to create a form- and force-fitting connection between components. This paper examines the characteristics of 3D printed pins in comparison to conventionally turned pins for heat staking applications. The 3D printed pins are created using fused layer modeling, with variations in horizontal and vertical building directions, as well as different layer thicknesses. The study investigates the impact of significant factors on the heat staking process, including the forming force and temperature. Tensile tests, micrographs, and micro-CT measurements were conducted to determine the properties of the heat-staked joints. Additionally, a stage plan was developed to enhance the understanding of the forming process of both printed and conventionally turned materials. The findings suggest that, under specific process parameters, 3D printed pins exhibit comparable strength to conventionally manufactured pins. The research also demonstrates that the anisotropy resulting from the layer-by-layer construction of the pins significantly influences the strength of the connection. Furthermore, the study reveals that 3D printed pins exhibit good forming accuracy during the heat staking process, and the cavities formed during printing can be substantially reduced. KW - Heat staking KW - Additive manufacturing KW - 3D printing KW - Material qualification KW - Polycarbonate (PC) KW - Fused layer modeling (FLM) Y1 - 2023 U6 - https://doi.org/10.1007/s00170-023-11850-y VL - 128 SP - 547 EP - 562 PB - Springer Nature ER - TY - PAT A1 - Maiwald, Frederik A1 - Hierl, Stefan T1 - Laser welding device for clamping and welding components and method for clamping and welding components Y1 - 2023 UR - https://data.epo.org/publication-server/rest/v1.0/publication-dates/20230830/patents/EP4234213NWA1/document.pdf ER - TY - JOUR A1 - Bartsch, Alexander A1 - Burger, Moritz A1 - Grad, Marius A1 - Esper, Lukas A1 - Schultheiß, Ulrich A1 - Noster, Ulf A1 - Schratzenstaller, Thomas T1 - Enhancement of laser cut edge quality of ultra-thin titanium grade 2 sheets by applying an in-process approach using modulated Yb:YAG continuous wave fiber laser JF - Discover Mechanical Engineering N2 - Titanium is used in many areas due to its excellent mechanical, biological and corrosion-resistant properties. Implants often have thin and filigree structures, providing an ideal application for fine cutting with laser. In the literature, the main focus is primarily on investigating and optimizing the parameters for titanium sheets with thicknesses greater than 1 mm. Hence, in this study, the basic manufacturing parameters of laser power, cutting speed and laser pulse of a 200 W modulated fiber laser are investigated for 0.15 mm thick grade 2 titanium sheets. A reproducible, continuous cut could be achieved using 90 W laser-power and 2 mm/s cutting-speed. Pulse pause variations between 85 and 335 μs in 50 μs steps and a fixed pulse width of 50 μs show that a minimum kerf width of 23.4 μm, as well as a minimum cut edge roughness Rz of 3.59 μm, is achieved at the lowest pulse pause duration. An increase in roughness towards the laser exit side, independent of the laser pulse pause duration, was found and discussed. The results provide initial process parameters for cutting thin titanium sheets and thus provide the basis for further investigations, such as the influence of cutting gas pressure and composition on the cut edge. KW - Laser cutting KW - Titanium sheet KW - Kerf Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-65647 N1 - Corresponding author: Alexander Bartsch IS - 10 PB - Springer ER - TY - INPR A1 - Grad, Marius A1 - Haag, Lydia A1 - Hahn, Konstantin A1 - Schultheiß, Ulrich A1 - Esper, Lukas A1 - Noster, Ulf T1 - Influence of carbon content on the formation of TiC at diffusion bonded titanium-steel interface N2 - Hot pressing of pure Ti and various carbon steels in a temperature range of 950 – 1050 °C creates an up to 9 μm thick compound layer of TiC at the Ti/ steel interface. The calculation of the activation energy for layer formation is 126.5 - 136.7 kJ/mol, independent of the steels carbon content. As the carbon content of the steel increases, the layer thickness also increases, which provides enormous potential for the surface modification of Ti/ Ti-alloys. Y1 - 2023 U6 - https://doi.org/10.2139/ssrn.4261928 PB - Elsevier ER - TY - INPR A1 - Burger, Moritz A1 - Bartsch, Alexander A1 - Grad, Marius A1 - Esper, Lukas A1 - Schultheiß, Ulrich A1 - Noster, Ulf A1 - Schratzenstaller, Thomas T1 - Enhancement of laser cut edge quality of ultra-thin titanium grade 2 sheets by applying in-process approach using modulated Yb:YAG continuous wave fibre laser N2 - Titanium is used in many areas due to its excellent mechanical, biological and corrosion-resistant properties. Implants often have thin and filigree structures, providing an ideal application for laser fine cutting. In literature, the main focus is primarily on investigating and optimizing the parameters for titanium sheet thicknesses greater than 1 mm. Hence, in this study, the basic manufacturing parameters of laser power, cutting speed and laser pulsing of a 200 W modulated fibre laser are investigated for 0.15 mm thick titanium grade 2 sheets. A reproducible, continuous cut could be achieved using 90 W laserpower and 2 cutting-speed. Pulse pause variations between 85–335 μs in 50 μs steps and fixed pulse duration of 50 μs show that a minimum kerf width of 23.4 μm, as well as a minimum cut edge roughness Rz of 3.59 μm, is achieved at the lowest pulse pause. An increase in roughness towards the laser exit side, independent of the laser pulse pause, was found and discussed. The results provide initial process parameters for cutting thin titanium sheets and thus provide the basis for further investigations, such as the influence of cutting gas pressure and composition on the cut edge. Y1 - 2023 U6 - https://doi.org/10.21203/rs.3.rs-2520041/v1 N1 - Erschienen in der Zeitschrift: Discover Mechanical Engineering, https://opus4.kobv.de/opus4-oth-regensburg/frontdoor/index/index/docId/6564 ER - TY - GEN A1 - Esper, Lukas A1 - Noster, Ulf A1 - Schultheiss, Ulrich A1 - Bund, Andreas T1 - Quasi-in-Situ Analysis of Electropolished Additively Manufactured Stainless Steel Surfaces T2 - ECS Meeting Abstracts, F01: Advances in Industrial Electrochemistry and Electrochemical Engineering N2 - Progress in additive manufacturing is leading to the emergence of new areas of application. Laser Powder Bed Fusion (L-PBF) is increasingly used for the development of metallic medical implants, but for high-risk implants like vascular support structures (stents), surface quality is critical to ensure successful implantation without harming the surrounding tissue and ensure the patients’ health. Therefore, enhancing the surface quality is crucial. Electropolishing is a method for removing surface roughness by smoothing out micro-peaks and valleys. However, L-PBF structures have a high surface roughness due to metal particles adhering on the surface. To achieve a smooth surface for additively manufactured implants like stents using electropolishing, the removal of these particles needs to be studied in more detail. The objective of this study is to examine the electropolishing mechanism of 316L stainless steel samples additively manufactured through Laser Powder Bed Fusion (L-PBF). The main objective is to investigate the removal properties and surface characteristics during electropolishing. To achieve this, various surfaces were characterized for morphology and roughness during Hull cell experiments. Markings are utilized on the Hull cell sample surfaces to identify points of interest during quasi-in-situ measurements. The surfaces are then analyzed after multiple time steps, applying different currents to investigate particle dissolution. The surface characteristics are analyzed through scanning electron microscopy, and surface roughness is analyzed using laser scanning microscopy. The results show that the electropolishing process preferentially removes the adhering particles present on the surface of the samples. Increasing the current density results in faster particle dissolution and a smoother surface (see Figure 1a and b). The mechanism of material removal of various surface features, as shown in Figure 1 (red circle, yellow arrow and red square), was assessed based on the experimental results of the surface structures seen on the SEM images. It was found that different surface features were removed during the experiment at different polishing times and current densities. The amount of charge flowed was found to correlate with surface morphology. Based on the obtained results, various surface features (such as large adherent particles, agglomerates of smaller particles, and valleys) and their changes with increasing test duration and current density were observed by quasi-in situ analyses. A reduction in the diameter of round particles adhering to the surface was observed at both low and higher current densities (see Figure 1a red circle a). Increasing the polishing time resulted in leveling of both large particles and valleys (see Figure 1b red square). Also, dissolution of agglomerates of smaller particles occurred at different polishing times as a function of current density and polishing time (see Figure 1a yellow arrow) are observed. Smoothed surface structures can be observed in regions with equivalent surface charge density (see Figure 2). As a result, comparable surface morphologies may appear at the same area charge density, irrespective of a specific current density. So, it may be adequate to only consider the amount of charge flowed to describe the electropolishing of additive materials. In conclusion, comprehending the dissolution characteristics of particles on L-PBF surfaces is essential for attaining satisfactory surface finish in electropolishing. The results of this study offer valuable perspectives into the electropolishing mechanism of additively manufactured 316L stainless steel and can guide future investigations on surface finishing and polishing of additive manufactured implants like stents. Figure 1 KW - General Earth and Planetary Sciences KW - General Environmental Science Y1 - 2023 U6 - https://doi.org/10.1149/MA2023-02241342mtgabs SN - 2151-2043 VL - MA2023-02 SP - 1342 EP - 1342 PB - The Electrochemical Society ER -