TY - JOUR A1 - Burdin, Dmitrii A. A1 - Ekonomov, Nikolai A. A1 - Chashin, Dmitri V. A1 - Fetisov, Leonid Y. A1 - Fetisov, Yuri K. A1 - Shamonin (Chamonine), Mikhail T1 - Temperature Dependence of the Resonant Magnetoelectric Effect in Layered Heterostructures JF - Materials N2 - The dependence of the resonant direct magnetoelectric effect on temperature is studied experimentally in planar composite structures. Samples of rectangular shapes with dimensions of 5 mm x 20 mm employed ferromagnetic layers of either an amorphous (metallic glass) alloy or nickel with a thickness of 20-200 m and piezoelectric layers of single crystalline langatate material or lead zirconate titanate piezoelectric ceramics with a thickness of 500 m. The temperature of the samples was varied in a range between 120 and 390 K by blowing a gaseous nitrogen stream around them. It is shown that the effective characteristics of the magnetoelectric effectsuch as the mechanical resonance frequency f(r), the quality factor Q and the magnitude of the magnetoelectric coefficient (E) at the resonance frequencyare contingent on temperature. The interrelations between the temperature changes of the characteristics of the magnetoelectric effect and the temperature variations of the following material parametersYoung's modulus Y, the acoustic quality factor of individual layers, the dielectric constant epsilon, the piezoelectric modulus d of the piezoelectric layer as well as the piezomagnetic coefficients ((n)) of the ferromagnetic layerare established. The effect of temperature on the characteristics of the nonlinear magnetoelectric effect is observed for the first time. The results can be useful for designing magnetoelectric heterostructures with specified temperature characteristics, in particular, for the development of thermally stabilized magnetoelectric devices. KW - acoustic quality factor KW - composite structure KW - linear KW - magnetoelectric effect KW - magnetoelectric heterostructure KW - magnetostriction KW - nonlinear KW - piezoelectric KW - temperature dependence Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-32185 N1 - corresponding author: Mikhail Shamonin VL - 10 IS - 10 PB - MDPI ER - TY - JOUR A1 - Savelev, Dmitrii V. A1 - Glavan, Gašper A1 - Belan, Viktoria O. A1 - Belyaeva, Inna A. A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail T1 - Resonant Magnetoelectric Effect at Low Frequencies in Layered Polymeric Cantilevers Containing a Magnetoactive Elastomer JF - Applied Sciences N2 - In this work, the resonance enhancement of magnetoelectric (ME) coupling at the two lowest bending resonance frequencies was investigated in layered cantilever structures comprising a magnetoactive elastomer (MAE) slab and a commercially available piezoelectric polymer multilayer. A cantilever was fixed at one end in the horizontal plane and the magnetic field was applied horizontally. Five composite structures, each containing an MAE layer of different thicknesses from 0.85 to 4 mm, were fabricated. The fundamental bending resonance frequency in the absence of a magnetic field varied between roughly 23 and 55 Hz. It decreased with the increasing thickness of the MAE layer, which was explained by a simple theory. The largest ME voltage coefficient of about 7.85 V/A was measured in a sample where the thickness of the MAE layer was ≈2 mm. A significant increase in the bending resonance frequencies in the applied DC magnetic field of 240 kA/m up to 200% was observed. The results were compared with alternative designs for layered multiferroic structures. Directions for future research were also discussed. KW - flexible composite KW - low frequency KW - magnetoactive elastomer KW - magnetoelectric effect KW - piezoelectric polymer Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-30637 N1 - corresponding authors: Dmitry V. Saveliev and Mikhail Shamonin VL - 12 IS - 4 SP - 1 EP - 13 PB - MPDI ER - TY - JOUR A1 - Fetisov, Yuri K. A1 - Chashin, Dmitri V. A1 - Savelev, Dmitrii V. A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail T1 - Anisotropic Magnetoelectric Effect in a Planar Heterostructure Comprising Piezoelectric Ceramics and Magnetostrictive Fibrous Composite JF - Materials N2 - The direct magnetoelectric (ME) effect is investigated in a planar structure comprising mechanically coupled layers of a magnetostrictive fibrous composite (MFC) and a piezoelectric ceramics (lead zirconate titanate, PZT). The MFC is an array of Ni-wires with a diameter of 200 mu m that are aligned parallel to each other in a single layer. The wires are separated by a distance of 250 or 500 mu m and fixed in a polyamide matrix. The structure was placed in a tangential constant field H and was excited by an alternating magnetic field h parallel to H, while the voltage generated by the PZT layer was measured. The resulting field dependences of the magnetization M(H) and the magnetostriction lambda(H) were determined by the orientation of the field H in the plane of the structure and the distance between the Ni-wires. The ME coupling coefficient of the structure decreased from 4.8 to 0.25 V/A when the orientation of H was changed from parallel to perpendicular to Ni-wires. With an increase in the excitation field amplitude h, a nonlinear ME effect in the output voltage, namely frequency doubling, was observed. The frequency and field dependences of the efficiency of the ME transduction in the MFC-piezoelectric heterostructure are well described by the existing theory. KW - composite KW - frequency doubling KW - heterostructure KW - magnetoelectric effect KW - magnetostrictive fiber KW - piezoelectric ceramic material Y1 - 2019 U6 - https://doi.org/10.3390/ma12193228 N1 - Corresponding authors: Yuri Fetisov, Mikhail Shamonin VL - 12 IS - 19 SP - 1 EP - 13 PB - MDPI CY - Basel ER -