TY - JOUR A1 - Bartsch, Alexander A1 - Burger, Moritz A1 - Grad, Marius A1 - Esper, Lukas A1 - Schultheiß, Ulrich A1 - Noster, Ulf A1 - Schratzenstaller, Thomas T1 - Enhancement of laser cut edge quality of ultra-thin titanium grade 2 sheets by applying an in-process approach using modulated Yb:YAG continuous wave fiber laser JF - Discover Mechanical Engineering N2 - Titanium is used in many areas due to its excellent mechanical, biological and corrosion-resistant properties. Implants often have thin and filigree structures, providing an ideal application for fine cutting with laser. In the literature, the main focus is primarily on investigating and optimizing the parameters for titanium sheets with thicknesses greater than 1 mm. Hence, in this study, the basic manufacturing parameters of laser power, cutting speed and laser pulse of a 200 W modulated fiber laser are investigated for 0.15 mm thick grade 2 titanium sheets. A reproducible, continuous cut could be achieved using 90 W laser-power and 2 mm/s cutting-speed. Pulse pause variations between 85 and 335 μs in 50 μs steps and a fixed pulse width of 50 μs show that a minimum kerf width of 23.4 μm, as well as a minimum cut edge roughness Rz of 3.59 μm, is achieved at the lowest pulse pause duration. An increase in roughness towards the laser exit side, independent of the laser pulse pause duration, was found and discussed. The results provide initial process parameters for cutting thin titanium sheets and thus provide the basis for further investigations, such as the influence of cutting gas pressure and composition on the cut edge. KW - Laser cutting KW - Titanium sheet KW - Kerf Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-65647 N1 - Corresponding author: Alexander Bartsch VL - 2 IS - 10 PB - Springer ER - TY - JOUR A1 - Wiesent, Lisa A1 - Schultheiß, Ulrich A1 - Lulla, Philipp A1 - Nonn, Aida A1 - Noster, Ulf T1 - Mechanical properties of small structures built by selective laser melting 316 L stainless steel – a phenomenological approach to improve component design JF - Materials Science & Engineering Technology JF - Materialwissenschaft und Werkstofftechnik N2 - Experimental investigations are conducted to quantify the influence of specimen thickness and orientation on the mechanical properties of selective laser melted stainless steel 316 L. The results indicate that the mechanical strength and ductility increase with increasing specimen thickness until a saturation value is reached from a specimen thickness of about 2 mm. Specimen orientation dependency is pronounced for thin specimens (<1.5 mm), whereas only small deviations in strength are observed for thicker specimens with orientations of 30°, 45° and 90° to build direction. The mechanical properties of the specimen orientation of 0° to build direction shows great deviation to the other orientations and the smallest overall strength. A reliable design of selective laser melted components should account for specimen thickness and orientation, e. g. by a correction factor. Furthermore, it is recommended to avoid loads vertical (90°) and parallel (0°) to build direction to guarantee higher ductility and strength. T2 - Mechanische Eigenschaften von kleinen Strukturen aus selektiv lasergeschmolzenem 316 L Edelstahl – ein phänomenologischer Ansatz zur Verbesserung des Bauteildesigns Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-14718 N1 - Corresponding author: Lisa Wiesent VL - 51 IS - 12 SP - 1615 EP - 1629 PB - Wiley ER -