TY - JOUR A1 - Schwarz, Tobias A1 - Pastötter, Angelina A1 - Tran, T. H. A1 - Schlosser, Marc A1 - Kaulen, Corinna A1 - Lechner, Alfred A1 - Slabon, A. A1 - Kammler, Martin T1 - Effect of temperature on the growth of Cupric and Cuprous Nanoparticles in a wet chemical synthesis JF - Materials Letters N2 - Cuprous oxide (Cu2O) and cupric oxide (CuO) particles were synthesized using a wet chemical surfactant free method at different synthesis temperatures from 25 °C to 60 °C. Morphology, size, and chemical composition of the prepared Cu2O particles were analyzed by FESEM, PXRD, and UV-vis. We discovered that the chemical composition of the Cu2O particles remained unaffected by the synthesis temperature. However, morphology and size of the particles showed a strong temperature dependency. This could be attributed to the temperature induced formation of CuO species from the copper hydroxide (Cu(OH)2) precursor which also functions as copper precursor for the Cu2O particle growth. The cupric oxide species was determined to be the main cause for the formation of micrometer sized particles, whereas with the Cu(OH)2 precursor species for the Cu2O particles nanocubes with smaller edge lengths as well as octahedrons were obtained. KW - Crystal structure KW - Crystal growth KW - Nanoparticle KW - Copper oxide Y1 - 2025 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-79279 VL - 381 PB - Springer Nature ER - TY - JOUR A1 - Wolfgramm, Alex A1 - Abb, Valerius A1 - Samp, Artur A1 - Samp, Rafal A1 - Hoffmann, Jens Christoph A1 - Müller, Rainer A1 - Kammler, Martin T1 - Structural and functional evolution of HKUST-1 nanoparticles induced by ball milling JF - Next Materials N2 - In this study, the effect of post-synthetic ball milling on the structural and functional properties of as-synthesized nanoparticles of the copper-based metal-organic framework (MOF) HKUST-1 was investigated for the first time. Nanoparticles were synthesized using sodium formate as a capping agent. The crystalline particles were subjected to a controlled ball milling process, which induced significant structural changes. Powder X-ray diffraction (PXRD) revealed a reduction in crystallite size from 91 nm to 21 nm and the introduction of microstrain, partially disrupting the MOF's long-range crystalline order, as evidenced by peak broadening and the diminished intensity of high-angle reflections. Particle morphology pre- and post-milling was further studied with scanning electron microscopy (SEM) imaging, verifying a narrow particle size distribution of ± 22 nm after milling. Fourier-transform infrared spectroscopy (FTIR) indicated protonation of carboxylate groups in the larger pores of the framework, likely due to moisture incorporation during milling. Brunauer-Emmett-Teller (BET) surface area analysis showed a substantial decrease in specific surface area from 521 m²/g to 226 m²/g, suggesting a partial collapse of the porous framework. We discuss the applicability of ball milling as a versatile means of post-synthetic approach to reduce MOF particle sizes, a key element in the preparation of MOF-based thin films using inks or polymers. KW - Ball milling KW - Copper-based metal-organic framework KW - HKUST-1 KW - Nitrogen adsorption Y1 - 2026 U6 - https://doi.org/10.1016/j.nxmate.2025.101544 N1 - Corresponding author der OTH Regensburg: Alex Wolfgramm VL - 10 PB - Elsevier ER -