TY - CHAP A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Field emission from black silicon structures with integrated gate electrode T2 - 29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada N2 - Black silicon structures with integrated gate electrode were realized by using an improved fabrication process. An enhanced insulation layer was achieved by a combination of dry and wet oxidation, and a gold layer was evaporated as gate electrode. The black silicon structures were prepared with a RIE/ICP etching process at room temperature. Arrays of 16 and 100 apertures with buried p-doped black silicon whiskers have been fabricated. These structures have an emitter height of approximately 1.5 μm with tip radii between 5 nm and 30 nm. The whiskers are surrounded by the gate electrode in a distance of 1.5 μm. Integral field emission measurements yielded an onset voltage of 92 V for 16 apertures and 60 V for 100 apertures for an emission current of 1 nA. Maximum emission currents up to 0.2 μA were observed for the array with 100 apertures at a cathode voltage of 200 V. Stability measurements showed a current fluctuation of ± 21% at a mean value of the emission current of 12 nA over a period of 30 minutes for 16 apertures with b-Si whiskers. KW - field emission KW - black silicon KW - integrated gate electrode Y1 - 2016 U6 - https://doi.org/10.1109/IVNC.2016.7551532 SN - 2380-6311 SP - 219 EP - 220 PB - IEEE ER - TY - CHAP A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Benzocyclobutene as a novel integrated spacer material in a field emission electron source T2 - International Vacuum Nanoelectronics Conference (IVNC), 30th, 2017, Regensburg N2 - For the realization of a miniaturized field emission electron source we tested benzocyclobutene (BCB) as a new spacer material between cathode and anode. We fabricated black silicon emitters and characterized the emission behavior with an integrated 5 μm thin and large-area spacer of BCB. The integrated BCB layer allows the realization of a compact electron source with only two components consisting of a cathode with BCB and a grid. The comparison with other spacer materials like polyimide (25 μm thickness) or mica (50 μm thickness) revealed for the cathode with BCB a significantly reduced operational voltage of 240 V for a field emission current of 1 μA. KW - field emission KW - benzocyclobutene KW - integrated spacer KW - electron source KW - black silicon Y1 - 2017 U6 - https://doi.org/10.1109/IVNC.2017.8051605 SP - 192 EP - 193 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Müller, F. A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter T1 - Enhanced field emission from p-doped black silicon on pillar structures T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars. KW - black silicon KW - CATHODES KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - Iron KW - silicon KW - Vacuum technology Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225547 SP - 104 EP - 105 PB - IEEE ER - TY - CHAP A1 - Serbun, Pavel A1 - Porshyn, Vitali A1 - Müller, Günter A1 - Lützenkirchen-Hecht, Dirk A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Field emission behavior of single n- and p-type black Si pillar structures T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - We have investigated the properties of single n- and p-type black silicon (b-Si) pillars with a height of 20 μ m under strong electric field and halogen lamp or laser illumination. For both type of b-Si pillar structures, I-V measurements revealed strong activation effects, which consisted in sudden current increases during the first up/down voltage sweeps. The maximum reproducible emission current from a single n-type b-Si pillar structure was about 15 μ A. A pronounced saturation region at 240 nA was observed for a single p-type b-Si pillar. The current fluctuation over time showed a standard deviation of 28% and 2.5% for n- and p-type single b-Si pillar structures, respectively. Optical switching under halogen lamp illumination resulted in at least 3 times higher saturation currents and showed a linear dependence of the FE current on the laser power. KW - field emission KW - black silicon KW - photoemission Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520292 PB - IEEE ER -