TY - CHAP A1 - Edler, Simon A1 - Hansch, Walter A1 - Prommesberger, Christian A1 - Schreiner, Rupert T1 - Influence of adsorbates on the performance of a field emitter array in a high voltage triode setup T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - The influence of residual gas pressure on the characteristics of black-Silicon field emitter arrays in a high voltage triode setup is investigated. I-Vcharacteristics at different pressure levels show a decrease of emission current with rising pressure. This can be explained by an increase of the work function and charging of the emitter surface due to adsorbates. The initial characteristics can be restored by heating the FEA up to 110 °C during electron emission. This regeneration procedure enables an extension of the lifetime from about 20 h to 440 h at a residual gas pressure of 10 -5 mbar. KW - semiconductor field emission KW - field emitter array KW - silicon tips KW - emission current stability Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520214 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Hausladen, Matthias A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Bachmann, Michael A1 - Düsberg, Felix A1 - Pahlke, Andreas A1 - Shamonin (Chamonine), Mikhail A1 - Schreiner, Rupert T1 - Field emission current investigation of p-type and metallized silicon emitters in the frequency domain T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - We investigated two different field emitter arrays consisting of 10×10 p-type and 10×10 undoped Au-coated high aspect ratio silicon tips. The I-V characterization of the p-type sample showed a pronounced saturation for voltages higher than 500 V and a maximum emission current of 39 nA. The metallized sample revealed a FN-like emission up to several μA. The metallized and the p-type sample operating below the saturation region showed high current fluctuations of ±16%. Whereas, the metallized sample with current regulation and the p-type sample in the saturation yielded a current stability of ±0.4% and ±0.3%, respectively. Investigations in the frequency domain revealed the for field emission typical 1/f-noise. By operating in the saturation region (p-type sample) or using an emission current regulation (metallized sample) the noise level was reduced by at least 20 dB. Finally, the p-type sample was illuminated by a light emitting diode to increase and modulate the emission current in the saturation region. The emission current was increased by a factor of 3.7 to 145 nA. With this configuration we emulated an unstable emission behavior and evaluated the performance of our emission current regulation circuit. KW - field emission KW - field emitter array KW - silicon tip KW - current fluctuation KW - current stability KW - field emission noise Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520127 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert A1 - Huang, Yifeng A1 - She, Juncong T1 - Gated p-Si field emission cathode applied in an ionization vacuum gauge T2 - 29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada N2 - A commercial Bayard-Alpert ionization vacuum gauge was equipped with a field emission electron source based on a cathode consisting of an array of 16 gated, p-doped, and DLC-coated Si-tips and characterized. An anode current of about 1.3 μA led to an ion current of 7 fA at 3×10 -7 mbar and 0.8 pA at 4×10 -5 mbar. Whereas at pressures higher than 4×10 -5 mbar the emission current of the electron source decreased, the ratio of ion and anode current remained linear. A nearly constant sensitivity of ~ 17 mbar -1 of the ionization vacuum gauge within the investigated pressure range was depicted. KW - field emission KW - field emitter array KW - Si KW - DLC KW - electron source KW - ionization vacuum gauge Y1 - 2016 U6 - https://doi.org/10.1109/IVNC.2016.7551500 SN - 2380-6311 SP - 145 EP - 146 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Dams, Florian A1 - Serbun, Pavel A1 - Bachmann, Michael A1 - Müller, Günter A1 - Schreiner, Rupert T1 - High aspect ratio silicon tip cathodes for application in field emission electron sources T2 - 2014 27th International Vacuum Nanoelectronics Conference (IVNC), 6-10 July 2014, Engelberg, Switzerland N2 - Precisely aligned arrays of sharp tip structures on top of elongated pillars were realized by using an improved fabrication process including an additional inductively-coupled-plasma reactive-ion etching step. Arrays of n-type and p-type silicon with 271 tips have been fabricated and investigated. Those structures have a total height of 5–6 µm and apex radii less than 20nm. Integral field emission measurements of the arrays yielded low onset-fields in the range of 8–12V=µm and field enhancement factors between 300 and 700. The I-E curves of n-type structures showed the usual Fowler-Nordheim behaviour, whereas p-type structures revealed a significant saturation region due to the limited number of electrons in the conduction band and a further carrier depletion effect caused by the pillar. The maximum integral current in the saturation region was 150 nA at fields above 30V=µm. An excellent stability of the emission current of less than ± 2% fluctuation was observed in the saturation region. For n-type Si a maximum integral current of 10 µA at 24V=µm and an average current stability with a fluctuation of ± 50% were measured. KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - GEOMETRY KW - Iron KW - Sensor arrays KW - silicon KW - silicon tip Y1 - 2014 U6 - https://doi.org/10.1109/IVNC.2014.6894824 SP - 222 EP - 223 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Dams, Florian A1 - Bachmann, Michael A1 - Schreiner, Rupert T1 - Fabrication and simulation of silicon structures with high aspect ratio for field emission devices T2 - 2014 27th International Vacuum Nanoelectronics Conference (IVNC), 6-10 July 2014, Engelberg, Switzerland N2 - To obtain higher field enhancement factors of Si-tip structures, we present an improved fabrication process utilizing reactive-ion etching (RIE) with an inductively coupled plasma (ICP). In our design, a pillar under the tips is realized by a combination of RIE with ICP. With adjusted power settings (≈ 240 W) and step times (<; 5 s), vertical slopes with a low roughness of approximately 10 nm to 20 nm are possible. The remaining silicon is oxidized thermally to sharpen the emitters. A final tip radius of R <; 20 nm is obtained for the tips of the emitters. The pillar height HP can be mainly adjusted by the duration of the ICP-etching step. A total emitter height of H ≈ 6 μm with a pillar height of HP ≈ 5 μm is achieved. Simulations with COMSOL Multiphysics® are applied to calculate the field enhancement factor β. A two-dimensional model is used in rotational symmetry. In addition to the previous model, a pillar with a varying diameter ØP and height HP is added. A conventional emitter (H = 1 μm and R = 20 nm) placed on a pillar of the height HP ≈ 5 μm approximately results in a three times higher β-factor (β≈ 105). By decreasing the diameter ØP a slight increase of the β-factor is observed. However, the aspect ratio of the emitter mainly influences on the β-factor. KW - Anodes KW - CATHODES KW - FABRICATION KW - field emission KW - field emitter array KW - field enhancement factor KW - Iterative closest point algorithm KW - Lead KW - silicon tips Y1 - 2014 U6 - https://doi.org/10.1109/IVNC.2014.6894805 SP - 193 EP - 194 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Müller, F. A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter T1 - Enhanced field emission from p-doped black silicon on pillar structures T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars. KW - black silicon KW - CATHODES KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - Iron KW - silicon KW - Vacuum technology Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225547 SP - 104 EP - 105 PB - IEEE ER - TY - CHAP A1 - Bachmann, Michael A1 - Dams, Florian A1 - Düsberg, F. A1 - Hofmann, Martin A1 - Pahlke, Andreas A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Schreiner, Rupert T1 - Stability investigation of high aspect ratio n-type silicon field emitter arrays T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Electron sources based on silicon field emitter arrays, produced in processes based on semiconductor technology, are good candidates for a miniaturized X-ray source. A key parameter for this application is the stability of the X-ray photon flux and, thus, the emission current. In the present work we have investigated the influence of the residual gas pressure and a resistor in series on the emission stability of a high aspect ratio n-type silicon emitter array with hybrid extraction electrode. An increase of current fluctuations was found for pressures above 10-6 mbar. High resistances in series to the emitter array alter the emission characteristics, but greatly suppress spikes in the emission current and improve its stability. This, however, strongly depends on the bias point. The field enhancement factor is not affected by the resistance. In a long term measurement the emission current was found to be constant after an initial phase of degradation. KW - Current measurement KW - emission current stability KW - field emitter array KW - Field emitter arrays KW - RESISTANCE KW - Resistors KW - semiconductor field emission KW - silicon KW - silicon tips KW - Stability analysis KW - Thermal stability KW - XRF spectroscopy Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225584 SP - 204 EP - 205 PB - IEEE ER -