TY - JOUR A1 - Kleshch, Victor I. A1 - Serbun, Pavel A1 - Lützenkirchen-Hecht, Dirk A1 - Orekhov, Anton S. A1 - Ivanov, Victor E. A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Schreiner, Rupert A1 - Obraztsov, Alexander N. T1 - A Comparative Study of Field Emission from Pristine, Ion-treated and Tungsten Nanoparticle-decorated p-type Silicon Tips JF - Physica Status Solidi B N2 - The field electron emission characteristics of individual tips of a silicon field emitter array are analyzed. The array of conical‐shaped tips is fabricated on a p‐type silicon wafer by using reactive ion etching and sharpening oxidation. The tips are decorated with single tungsten nanoparticles at their apexes. Furthermore, the focused ion beam is also used to increase surface conductivity of some of the tips. Comparative measurements of field emission are performed by using the scanning anode probe field emission microscopy technique. All types of tips demonstrated emission activation consisting of a sudden current increase at a certain value of the applied voltage. Compared to the pristine tips, a noticeable reduction of the saturation effect in the current–voltage characteristics and a smaller light sensitivity for the decorated tips is found. For ion‐treated tips, saturation effects and light sensitivity are completely suppressed. Scanning electron microscopy observations reveal the formation of single nanoscale protrusions extending from the metal particles and from the apexes of bare ion‐treated tips after exposure under strong electric fields during the field emission measurements. The influence of protrusions growth on characteristics of silicon field emitter arrays is discussed. Y1 - 2019 U6 - https://doi.org/10.1002/pssb.201800646 VL - 256 IS - 9 PB - Wiley ER - TY - CHAP A1 - Kleshch, Victor I. A1 - Serbun, Pavel A1 - Orekhov, Anton A1 - Lützenkirchen-Hecht, Dirk A1 - Obraztsov, Alexander N. A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Schreiner, Rupert A1 - Lutzenkirchen-Hecht, Dirk T1 - Field emission properties of p-type silicon tips decorated with tungsten nanoparticles T2 - 2017 30th International Vacuum Nanoelectronics Conference (IVNC), 10-14 July 2017, Regensburg, Germany N2 - An array of conical-shaped p-type silicon tips was fabricated by using reactive ion etching and sharpening oxidation. The apex of each tip was decorated by a tungsten hemispherical nanoparticle. Field emission properties of the tips were measured by a tungsten-needle anode positioned above the tip apex. Tips decorated with tungsten nanoparticles demonstrated a smaller saturation region in current-voltage characteristics compared to the pristine tips. An emission activation process, which consisted in sudden current increase at certain value of applied voltage, was observed for the decorated silicon tips. This behavior was explained by the formation of vertical protrusions extending from the metal particles revealed by scanning electron microscopy after field emission experiments. KW - Current measurement KW - field emission KW - Ions KW - Iron KW - metal nanoparticles KW - nanoparticles KW - p-type silicon KW - Scanning electron microscopy KW - silicon KW - Tungsten Y1 - 2017 U6 - https://doi.org/10.1109/IVNC.2017.8051580 SP - 138 EP - 139 PB - IEEE ER -