TY - CHAP A1 - Navitski, Aliaksandr A1 - Serbun, Pavel A1 - Müller, Güntner A1 - Schreiner, Rupert A1 - Dams, Florian T1 - Efficient and reliable field emission from silicon tip arrays for miniaturized electron sources T2 - 2011 24th International Vacuum Nanoelectronics Conference ; 18-22 July 2011 Wuppertal N2 - Silicon-based cathodes with precisely aligned field emitter arrays (FEA) applicable for miniaturized electron sources were successfully developed and fabricated. The cathode chips contain about 3×105 Si tips/cm2 in a triangular array with a tip height of 2.5 μm, tip radius of 20 nm, and lateral distance between tips of 20 μm. Amazingly homogeneous and well-aligned field emission (FE) from all tips (i.e. 100% efficiency) and maximum stable currents of typically 0.1 μA for p- and 0.6 μA for n-type Si were reproducibly achieved. Current-voltage characteristics of p-type Si tips exhibit the expected saturation at around 10 nA due to limited supply of electrons from a depletion layer, while the n-type Si tips show the usual FN behaviour. Additional coating of the Si tips with a 10 nm Au layer resulted in at least 5 times higher average FE current levels i.e. typically 3 μA but lead, however, to a 30% increase of the onset voltage. KW - cathodes KW - coatings KW - elemental semiconductors KW - field emission KW - field emitter arrays KW - miniaturized electron sources KW - silicon tips KW - structured cold cathode Y1 - 2011 UR - https://ieeexplore.ieee.org/document/6004567?arnumber=6004567 SN - 978-3-00-035081-8 SN - 978-1-4577-1243-2 SN - 2380-6311 SN - 2164-2370 SP - 71 EP - 72 PB - IEEE CY - Piscataway, NJ ER - TY - CHAP A1 - Schreiner, Rupert A1 - Dams, Florian A1 - Prommesberger, Christian A1 - Bornmann, Benjamin A1 - Serbun, Pavel A1 - Navitski, Aliaksandr A1 - Müller, Güntner T1 - Silicon-based integrated field emission electron sources for sensor application T2 - 24th International Vacuum Nanoelectronics Conference (IVNC), 2011 : 18 - 22 July 2011, Wuppertal, Germany N2 - We report on the design, fabrication and characterization of p-type silicon field emitter arrays for the application in compact fast switchable electron sources. Since standard silicon technology has been used to prepare the devices, they can be easily integrated with other silicon based sensors and electronic components, too. The emitter arrays consist of approx. 3×105 tips per cm2, with a tip radius less than 20 nm. By using self-aligned processes, an integrated gate electrode with a diameter of  3 μm was placed concentrically around the tips. A mesh of silicon-beams with a grating period of 100 μm and beam width of 20 μm forms the anode of the electron source. A glass wafer (thickness 300 μm) acts as spacer between anode and Si-tip cathode. Characterization of the field emission properties of the emitter arrays was performed by high resolution field emission scanning microscopy. The emitter arrays exhibit a highly stable and very homogeneous emission. A maximum stable current of 0.1 μA per tip was found. A saturation level in the voltage current characteristics, which was found at around 10 nA, supports current stabilisation and will enable optical modulation of the emission current. KW - anodes KW - cathodes KW - field emission electron microscopy KW - field emission electron sources KW - field emitter arrays KW - silicon tips KW - structured cold cathode KW - vacuum sensors Y1 - 2012 UR - https://ieeexplore.ieee.org/document/6004541?arnumber=6004541 SP - 19 EP - 20 PB - IEEE CY - Piscataway, NJ ER - TY - CHAP A1 - Serbun, Pavel A1 - Navitski, Aliaksandr A1 - Müller, Güntner A1 - Schreiner, Rupert A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Dams, Florian T1 - Scaling of the field emission current from B-doped Si-tip arrays T2 - 25th International Vacuum Nanoelectronics Conference (IVNC) ; Jeju, Korea (South), 09.07.2012 - 13.07.2012 N2 - We have fabricated a test chip with various hexagonal arrays of B-doped Si tips (height ~ 3 μm, apex radius <; 30 nm, number 1-4447, resistivity 4 Ωcm, 100 orientation) in triangular arrangement (pitch 10 μm, density 1.16×10 6 cm -2 ) in order to systematically investigate the field emission current scaling with the number N of tips. Regulated voltage scans for 1 nA revealed rather efficient emission from nearly all tips of the arrays at an average field of 15 V/μm. The expected current plateau was always obtained at fields around 20 V/μm, but its width strongly increased with N. In this carrier depletion range, the single tip provided a much higher stability (<; 5%) of the current (2-3 nA) than at lower (>; 50 %) and higher currents (>; 30%). Integral current measurements of the hexagonal arrays resulted in a statistically improved current stability (<; 1%) but only a weak increase of the total current with N 0.28 yet. These results will be discussed with respect to the remaining inhomogeneity of the tips. KW - Anodes KW - B-doped KW - boron KW - Current measurement KW - current scaling KW - electron field emission KW - elemental semiconductors KW - field emitter arrays KW - Iron KW - Nonhomogeneous media KW - silicon KW - Voltage control Y1 - 2012 SN - 978-1-4673-1984-3 SN - 978-1-4673-1983-6 SN - 978-1-4673-1982-9 U6 - https://doi.org/10.1109/IVNC.2012.6316965 SN - 2380-6311 SN - 2164-2370 SP - 1 EP - 2 PB - IEEE CY - Piscataway, N.J. ER -